SABIC Innovative Plastics Lexan® LUX1832 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® LUX1832 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MFR=3.0; Branched extrusion grade for LED applications, UV stabilized; available in diffuse colors
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 94 % | 94 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.23 GPa | 323 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 101 MPa | 14600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.37 GPa | 344 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 8.07 J/cm | 15.1 ft-lb/in | ASTM D256 |
| 1.26 J/cm @Temperature -30.0 °C |
2.36 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 64.0 J | 47.2 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 67.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C @Thickness 6.40 mm |
286 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 145 °C | 293 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, 34-700 12K 2x2 Twill Reinforced
- Quantum Composites QC-7752 50% Glass Fiber Heat Resistant Polyester SMC (discontinued **)
- Materion BrushCAST® 275CT Fine Grain Casting Alloy (As Cast & Aged)
- Iran Petrochemical (PCC) GPPS 1160 Polystyrene
- SPHERE ONE EXTENDOSPHERESâ„¢ SL-150 Hollow Spheres
- Techmer ES Plastiblend® PC/ABS FR 6206 UV
- Unitika RUN35-C25 PA6, Conditioned
- A. Schulman POLYBATCH™ Treated Pine 60175U/4 Concentrate Based In LLDPE
- Arlon Thermabond® 99A50X008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- PPT BP780 NiZn Ferrite Powder
Copyright © lookpolymers.com All Rights Reserved