Amity Thermosets AMP 481 Phenolic Molding Organic and inorganic Filler, Compression Molded

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Amity Thermosets
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Amity Thermosets AMP 481 Phenolic Molding Organic and inorganic Filler, Compression Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics:Good tracking resistanceGood dielectric strengthGood electrical insulation Applications:Switchgear components which ought to have high tracking resistanceCircuit protecting switches Micro switches etc. Information provided by Amity Thermosets Limited

Physical Properties	Metric	English	Comments
Density	1.40 - 1.45 g/cc	0.0506 - 0.0524 lb/in³	Molding; IS 867-1963
Apparent Bulk Density	0.620 - 0.700 g/cc	0.0224 - 0.0253 lb/in³	IS 867-1963
Water Absorption	<= 0.40 %	<= 0.40 %	IS 13411-1993
Linear Mold Shrinkage	0.0040 - 0.0075 cm/cm	0.0040 - 0.0075 in/in	bar; IS 13411-1992
	0.0060 - 0.0075 cm/cm	0.0060 - 0.0075 in/in	disk; IS 13411-1992

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	56.0 - 70.0 MPa	8120 - 10200 psi	5 mm/min.; IS 867-1963
Shear Strength	75.0 - 90.0 MPa	10900 - 13100 psi	2mm/min.; IS 867-1963
Izod Impact, Notched	0.220 - 0.350 J/cm	0.412 - 0.656 ft-lb/in	IS 13411-1992

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 - 3.16e+11 ohm-cm	1.00e+11 - 3.16e+11 ohm-cm	IS 3396-1979
Surface Resistance	1.00e+10 - 1.00e+11 ohm	1.00e+10 - 1.00e+11 ohm	IS 3396-1979
Dielectric Strength	>= 7.00 kV/mm @Temperature 90.0 °C	>= 178 kV/in @Temperature 194 °F	IS 2584-1963
Comparative Tracking Index	>= 300 V	>= 300 V	2824-1975

Processing Properties	Metric	English	Comments
Mold Temperature	160 - 180 °C	320 - 356 °F
Injection Pressure	15.68 - 34.3 MPa	2274 - 4970 psi	Mold Pressure
Cure Time	0.417 - 0.583 min	0.00694 - 0.00972 hour	per mm
Shelf Life	4.00 Month	4.00 Month	10-25°C