Americas Styrenics STYRON® 665 High Heat Crystal Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Heat Resistant Grade |
| Manufacturer | Americas Styrenics LLC |
| Trade Name | STYRON® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Americas Styrenics STYRON® 665 High Heat Crystal Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product CharacteristicsAdditive freeFood Contact CompliantTypical ApplicationsFilmInformation provided by AmericasStyrenics LLC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 107 | 107 | ASTM D785 |
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D638 |
| Tensile Strength | 52.4 MPa | 7600 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 3.17 GPa | 460 ksi | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 3.21 GPa | 465 ksi | ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.3 °C | 209 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.9 °C | 192 °F | ASTM D648 |
| Vicat Softening Point | 108 °C | 227 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP RX06480 PA 66
- Stir SpA SR 94 T (PVC)
- Unipetrol PE HD LITEN® MB/ML 77 HDPE
- A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene
- A. Schulman POLYFORT™ FPP 3391 Chemically Coupled, Modified Polypropylene
- Hexcel® HexPly® 8551-7 Epoxy Matrix
- Azoty Tarnow™ Tarnamid® T-27 MW30 Polyamide 6 - Mineral Reinforced
- Samsung Cheil Industries Infino® CF-1030 PC, Unreinforced High Impact
Copyright © lookpolymers.com All Rights Reserved