- Alliance BIF-11 Bonded (Composite) Magnetic Material
Alliance BIF-11 Bonded (Composite) Magnetic Material
| Category | Ceramic , Metal , Electronic/Magnetic Alloy |
| Manufacturer | Alliance LLC |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Alliance BIF-11 Bonded (Composite) Magnetic Material.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.60 - 3.60 g/cc | 0.0939 - 0.130 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 30.0 - 80.0 MPa | 4350 - 11600 psi | |
| Modulus of Elasticity | 4.00 - 5.50 GPa | 580 - 798 ksi | |
| Flexural Strength | 50.0 - 100 MPa | 7250 - 14500 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 - 50.0 µm/m-°C @Temperature 20.0 °C |
16.7 - 27.8 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
| Specific Heat Capacity | <= 0.200 J/g-°C | <= 0.0478 BTU/lb-°F | |
| Maximum Service Temperature, Air | 150 °C | 302 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00 ohm-cm | >= 1.00 ohm-cm | |
| Magnetic Coercive Force, Hc | 2200 Oe | 2200 Oe | |
| 2900 Oe | 2900 Oe | Intrinsic | |
| Magnetic Remanence, Br | 2400 Gauss | 2400 Gauss | |
| Magnetic Maximum Energy Product, BH | 1.4 MGOe | 1.4 MGOe | |
| Curie Temperature | 450 °C | 842 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Reversible Temp Coef., Bd | -0.20 %/°C | |
| Reversible Temp Coef., Hd | +0.27 %/°C | |
| Temperature Coefficient, Br | -0.2 %/°C | (20-100°C) |
| Temperature Coefficient, Hci | +0.3 %/°C | (20-100°C) |
Users viewing this material also viewed the following:
- Plastcom SLOVASTYR® B BT N PBT
- Ineos Nova PS 3190 Crystal Polystyrene (discontinued **)
- Michelman® Michem® Lube 160PFP Anionic carnauba wax emulsion
- Solvay TECHNYL® C 52G4 MZ25 PA6, 25% mineral filler, DRY
- A. Schulman POLYBATCH™ Blue 4656 Concentrate Based In Polyethylene
- A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Fainplast Compounds Ethylplus 625 MD Polyethylene Cable Compound
- Akzo Nobel Expancel® 551 DU 80 Dry unexpanded microspheres
Copyright © lookpolymers.com All Rights Reserved