Alcoa KAMA 4200 RPET (discontinued **)

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Alcoa KAMA 4200 RPET (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

CapabilitiesGauge: .007” to .050” (178 to 1270µm)Width: 12” to 48” (305 to 1219mm)Core size: 6” standard, 3” and 8” availableRoll O.D.: 29” standard, available up to 40”Up to 100% recycled contentClear, tinted, and custom colors availableSilicone coating available4 strategic manufacturing locationsPropertiesEconomical alternative for clear packagingGood clarity and impact strength100% recyclableInformation provided by Alcoa Kama Co.

Physical Properties	Metric	English	Comments
Specific Gravity	1.33 g/cc	1.33 g/cc
Viscosity Measurement	>= 0.66	>= 0.66	Intrinsic Viscosity; ASTM D3835
Thickness	178 - 1270 microns	7.00 - 50.0 mil
Linear Mold Shrinkage	0.020 - 0.050 cm/cm	0.020 - 0.050 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	48.3 - 58.6 MPa	7000 - 8500 psi	ASTM D638
Elongation at Break	100 - 200 %	100 - 200 %	ASTM D638
Flexural Modulus	2.24 - 2.55 GPa	325 - 370 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	65.6 °C	150 °F
Minimum Service Temperature, Air	-12.2 °C	10.0 °F

Optical Properties	Metric	English	Comments
Haze	<= 4.0 %	<= 4.0 %	ASTM D1003
Transmission, Visible	>= 85 %	>= 85 %	ASTM D1003

Processing Properties	Metric	English	Comments
Processing Temperature	121 - 154 °C	250 - 310 °F	Thermoforming Temp

Descriptive Properties	Value	Comments
Clarity, %	>97
Resistance to Acid	Good to Excellent
Resistance to Alcohols	Good to Excellent
Resistance to Alkalis	Fair to Good
Resistance to Fat, Grease, and Oil	Good to Excellent
Resistance to Hydrocarbon Solvents	Good to Excellent
Resistance to Strong Oxidizers	Good to Excellent
Yield, in²/lb/mil	20810