- Adell RA-14 Copolymer Polypropylene, 20% Talc Filled
Adell RA-14 Copolymer Polypropylene, 20% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell RA-14 Copolymer Polypropylene, 20% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Adell Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 48 | 48 | ASTM D785 |
| Hardness, Rockwell R | 74 | 74 | ASTM D785 |
| Tensile Strength, Ultimate | 28.3 MPa | 4100 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Strength | 37.9 MPa | 5500 psi | ASTM D790 |
| Flexural Modulus | 1.70 GPa | 247 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.30 J/cm | 8.06 ft-lb/in | ASTM D256 |
| Gardner Impact | 3.40 J | 2.51 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Raschig Group MELOPAS® 6605 MP Melamine
- SABIC Innovative Plastics LNP LUBRICOMP AI001XXH ABS
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N650 Filler
- Kolon NOPLA® KE831 PEN-PET Copolyester
- Loxim 820 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant
- Mitsubishi Hostaphan® RN, 125 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- Monmouth Rubber & Plastics Durafoamâ„¢ S88 PVC/NBR
- Saint-Gobain CHR® A603 Aluminum Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- Akzo Nobel Expancel® 950 MB 120 Masterbatch with unexpanded microspheres
Copyright © lookpolymers.com All Rights Reserved