Addiplast Addilene J 490 M20F Flame Retardant Polypropylene, 20% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant , Polypropylene, Mineral Reinforced |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene J 490 M20F Flame Retardant Polypropylene, 20% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, mineral filled, with halogensInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183/A |
| Melt Flow | 10 g/10 min | 10 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | Conditioned; ISO 868 |
| Tensile Strength at Break | 21.0 MPa | 3050 psi | Conditioned; ISO R 527 |
| Elongation at Break | 11 % | 11 % | Conditioned; ISO R 527 |
| Modulus of Elasticity | 2.60 GPa | 377 ksi | Conditioned; ISO 178 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | Conditioned; ISO 180/1A |
| Charpy Impact Unnotched | 3.70 J/cm² | 17.6 ft-lb/in² | Conditioned; ISO 179/IeU |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ISO 75-2/AF |
| Vicat Softening Point | 151 °C | 304 °F | ISO 306/A50 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | Conditioned; CEI 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | Conditioned; CEI 60093 |
| Dielectric Strength | 43.0 kV/mm | 1090 kV/in | CEI 60243-1 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 21-8115 Polyamide 6/6T, with carbon fiber, lubricant modified
- Huntsman AroCy XU 71787.02 L Cyanate Ester
- Teknor Apex APEX® 3301-75 Polyvinyl Chloride, Flexible
- Total PPM H350 Polypropylene, Homopolymer Medical Grade
- ChevronTexaco ISO 150 Ultra Gear Lubricant
- ExxonMobil Exxtral™ BNT 010 Performance Polyolefin
- 3M GM613 Ultra Soft Gripping Material
- Arkema Group KYNAR FLEX® 3120-15 Polyvinylidene Fluoride Copolymer - Extrusion & Molding
- Bisalloy Steels BisPlate 500 Thickness 6-100 mm
Copyright © lookpolymers.com All Rights Reserved