- Adamas Adalon® 403 PTFE, 15% Polyimide
Adamas Adalon® 403 PTFE, 15% Polyimide
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Adamas |
| Trade Name | Adalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Adalon® 403 PTFE, 15% Polyimide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.90 - 1.98 g/cc | 1.90 - 1.98 g/cc | ASTM D792 |
| Deformation | 7.0 - 13 % | 7.0 - 13 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 57 - 64 | 57 - 64 | ASTM D2240 |
| Ball Indentation Hardness | 48.0 - 52.0 MPa | 6960 - 7540 psi | ISO 2032-N132 |
| Tensile Strength at Break | >= 16.0 MPa | >= 2320 psi | ASTM D4745-97 |
| Elongation at Break | >= 180 % | >= 180 % | ASTM D4745-97 |
| Compressive Strength | 6.50 - 8.50 MPa @Temperature 23.0 °C, Time 86400 sec |
943 - 1230 psi @Temperature 73.4 °F, Time 24.0 hour |
@ 1% deformation, 140 Kg/cm<sup>2</sup>; ASTM D621 |
| Coefficient of Friction, Dynamic | 0.10 - 0.15 | 0.10 - 0.15 | ASTM D1894 |
| Coefficient of Friction, Static | 0.18 - 0.42 | 0.18 - 0.42 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | ASTM C 177 |
| Melting Point | 327 °C | 621 °F | DSC |
| Maximum Service Temperature, Air | 250 °C | 482 °F | DSC |
| Minimum Service Temperature, Air | -85.0 °C | -121 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.00e+18 ohm-cm | 8.00e+18 ohm-cm | ASTM D257 |
| Surface Resistance | 6.00e+14 ohm | 6.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 1.8 @Frequency 60.0 - 2.00e+6 Hz |
1.8 @Frequency 60.0 - 2.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 - 50.0 kV/mm | 508 - 1270 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- MV Labs ND900 NdPO4·xH2O Neodymium phosphate hydrate
- Poco Graphite ACF-10Q Industrial Grade Graphite
- PolyOne Geon™ Vinyl Flexible 86280 Polyvinyl Chloride, Flexible (PVC, Flexible)
- 3M Dyneon™ TFM™ 1705 Modified PTFE Powder (discontinued **)
- Inno-Comp INNOPOL® CS 2-3110 TO BU 10% Talc Filled Polypropylene Copolymer
- A. Schulman POLYFORT™ FPP 2181HU High Flow, Fortified, Impact Resistant Polypropylene
- Loctite® Output™ 5404 Heat Cure Silicone
- Covestro Makrolon® 6555 Polycarbonate, Injection Grade
- Eurostar Staramide AG3 PA66, 15% Glass Filled, Injection Molded
- Braskem GP100BK HDPE High Density Extrusion Polyethylene
Copyright © lookpolymers.com All Rights Reserved