Styron INSPIRE™ TF3800 Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Styron |
| Trade Name | INSPIRE™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron INSPIRE™ TF3800 Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.136 g/cc | 1.136 g/cc | ASTM D792 |
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 230 °C |
21 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 11.8 MPa | 1710 psi | ASTM D638 |
| Tensile Strength, Yield | 16.3 MPa | 2360 psi | ASTM D638 |
| Elongation at Break | 33 % | 33 % | ASTM D638 |
| Elongation at Yield | 4.8 % | 4.8 % | ASTM D638 |
| Tensile Modulus | 1.19 GPa | 172 ksi | ASTM D638 |
| Flexural Strength | 22.2 MPa | 3220 psi | ASTM D790 |
| Flexural Modulus | 1.64 GPa | 238 ksi | ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm @Thickness 3.17 mm, Temperature -28.9 °C |
0.400 ft-lb/in @Thickness 0.125 in, Temperature -20.0 °F |
ASTM D256 |
| 0.427 J/cm @Thickness 3.17 mm, Temperature -17.8 °C |
0.800 ft-lb/in @Thickness 0.125 in, Temperature 0.000 °F |
ASTM D256 | |
| 3.26 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
6.10 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 27.0 J @Temperature 22.8 °C |
19.9 ft-lb @Temperature 73.0 °F |
ASTM D3763 |
| 31.0 J @Temperature -17.8 °C |
22.9 ft-lb @Temperature 0.000 °F |
ASTM D3763 | |
| 34.0 J @Temperature -28.9 °C |
25.1 ft-lb @Temperature -20.0 °F |
ASTM D3763 | |
| 34.0 J @Temperature -33.9 °C |
25.1 ft-lb @Temperature -29.0 °F |
ASTM D3763 | |
| Falling Dart Impact | 18.0 J | 13.3 ft-lb | 73°F, Peak Energy; ASTM D3763 |
| 22.0 J | 16.2 ft-lb | 0°F, Peak Energy; ASTM D3763 | |
| 24.0 J | 17.7 ft-lb | -20°F, Peak Energy; ASTM D3763 | |
| 24.0 J | 17.7 ft-lb | -29°F, Peak Energy; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 73.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.9 °C @Thickness 3.17 mm |
201 °F @Thickness 0.125 in |
Unannealed; ISO 75-2-92 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.1 °C @Thickness 3.17 mm |
124 °F @Thickness 0.125 in |
Unannealed; ISO 75-2-92 |
Users viewing this material also viewed the following:
- 3M Dyneon™ PFA 6525N Perfluoroalkoxy Fluorothermoplastic (discontinued **)
- Kazanorgsintez E-14 Petroleum Resin
- Lehmann & Voss LUVOCOM® 1850-7692 PBT, with glass spheres and PTFE
- Mitsubishi Xantar® G4F 22 UR Polycarbonate-20% Glass Reinforced
- Latrobe Nitralloy® N™ VAC-ARC Premium Nitriding Steel
- Lucas-Milhaupt Cerametil 716 Active Metal Brazing
- SABIC Innovative Plastics LNP LUBRICOMP EFL34HL PEI (Asia Pacific)
- DSM Akulon® K224-HG3 Nylon 6-15% Glass Reinforced (European and Asian Grade) (Dry)
- Diamond Polymers ABSPC 7030-HES ABS/PC Injection Molding Grade, High Impact
- Advanced Polymer Alloys Alcryn® 4670 NC Melt Processable Rubber
Copyright © lookpolymers.com All Rights Reserved