DuPont Elvaloy® 2116 AC Ethylene and 16% Ethyl Acrylate Copolymer

Category Polymer , Film , Thermoplastic
Manufacturer DuPont Packaging and Industrial Polymers
Trade Name Elvaloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Elvaloy® 2116 AC Ethylene and 16% Ethyl Acrylate Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Elvaloy® 2116 AC is intended for profile and tube extrusion. Its good chemical resistance, low temperature toughness and good flex life make it outstanding for specialty tubing. The material also is recommended for contour extrusion and for blow molding of toys, gaskets and other parts requiring permanent flexibility, stress cracking resistance and low temperature toughness. Elvaloy® 2116 AC also can be used in film applications where softness and flexibility are needed.Elvaloy® 2116 AC is easily processed on standard equipment used for low density polyethylene. It is very heat stable and does not give corrosive decomposition products during processing, even at the upper limit of the recommended temperature range.Information provided by DuPont.
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
ASTM D792 - ISO 1183
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238 - ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 88
88
ASTM D2240 - ISO 868
Hardness, Shore D 31
31
ASTM D2240 - ISO 868
Tensile Strength at Break 15.0 MPa
2180 psi
500 mm/min; ASTM D638 - ISO 527-2
Elongation at Break 690 %
690 %
500 mm/min; ASTM D638 - ISO 527-2
Tensile Modulus 0.0400 GPa
5.80 ksi
1 mm/min; ASTM D638 - ISO 527-2
Thermal Properties Metric English Comments
Melting Point 96.0 °C
205 °F
By DSC; ASTM D3418 - ISO 3146
Vicat Softening Point 60.0 °C
140 °F
A<sub>50</sub> (10N); ASTM D1525 - ISO 306
Processing Properties Metric English Comments
Rear Barrel Temperature 150 °C
302 °F
Extrusion lamination and extrusion coating
150 °C
302 °F
Cast film
150 °C
302 °F
Blown film
Middle Barrel Temperature 160 °C
320 °F
Blown film
210 °C
410 °F
Cast film
220 °C
428 °F
Extrusion lamination
Front Barrel Temperature 170 °C
338 °F
Blown film
250 °C
482 °F
Cast film
290 °C
554 °F
Extrusion lamination
Adapter Temperature 180 °C
356 °F
Blown film
250 °C
482 °F
Cast Film
290 °C
554 °F
Extrusion lamination
Die Temperature 180 °C
356 °F
Blown film
250 °C
482 °F
Cast film
290 °C
554 °F
Extrusion lamination
Melt Temperature 160 - 220 °C
320 - 428 °F
For blow molding
Descriptive Properties Value Comments
EA-Content 16 wt.%
DuPont Method