Aclo Accutech Polypropylene Homopolymer HP0339M30CL Mica Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0339M30CL Mica Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.111 g/cc | 0.04014 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | MD; ASTM D955 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 60 | 60 | ASTM D785 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 4.000 GPa | 580.1 ksi | ASTM D638 |
| Flexural Strength | 48.0 MPa | 6960 psi | ASTM D790 |
| Flexural Modulus | 4.500 GPa | 652.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.310 J/cm | 0.580 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.9 °C | 183 °F |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO FUSE SERIES 180 BLACK TOUGHENED (2400 Viscosity) Rapid Bonding Adhesive
- Ipiranga Petrochem PH 1310 Polypropylene
- Freudenberg Simrit N466 Nitrile Elastomer (NBR)
- Zircar Refractory Composites RS-99-45 Refractory Sheet
- Tra-Con Tra-Bond JL01 High Viscosity High Temperature Fiber Optic Adhesive
- Clariant 612-01 HSL Black Nylon 612, Heat Stabilized
- Ashley Polymers Ashlene® 990L-40G Nylon 610, 40% Glass Reinforced
- 3M FA023 Matte Clear Acetate Label Products
- Unifrax Fiberwall® Bonded 24 Bonded Module System
Copyright © lookpolymers.com All Rights Reserved