Aclo Accutech Polypropylene Homopolymer HP0336C40L Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336C40L Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.205 g/cc | 0.04353 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 86 | 86 | ASTM D785 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ASTM D638 |
| Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 |
| Flexural Modulus | 2.200 GPa | 319.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.750 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.2 °C | 144 °F |
Users viewing this material also viewed the following:
- Permabond 101 Cyanoacrylate, Wicking Viscosity
- Plenco 50015 PET, Pellet, Injection Molded, White (discontinued **)
- Kotec Carbotex KG-30F15 Polycarbonate, Wear Resistant, 30% Glass Fiber Reinforced
- Master Bond EP51FL-1 Rapid Curing Cryogenic Two Component Epoxy
- A. Schulman ComAlloy® E-13370 Lubricated Reinforced Polyester Alloy
- TIMCAL TIMREX® T15 Primary Synthetic Graphite
- Chosun Refractories ZR-C Special brick
- Chosun Refractories ASM-31 Air-Setting Mortar
- Formosa Plastics Formolene® L64220U Rotational Molding LLDPE (discontinued **)
- PSM Industries PolyAlloys MIM-430L sintered Soft Magnetic Steel
Copyright © lookpolymers.com All Rights Reserved