Sharadaa Ceramics REFCAST HA PLUS High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics REFCAST HA PLUS High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: We bring to our clients a qualitative range of Dense Alumina Castables that are conventional castable of medium purity. These castables cater to the application needs of various industries such as steel, cement, petrochemical and non-ferrous industries.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | >= 2.75 g/cc | >= 0.0994 lb/in³ | Dried at 110°C |
| Grain Size | <= 5000 µm | <= 5000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.00343 GPa @Temperature 1100 °C |
0.497 ksi @Temperature 2010 °F |
|
| 0.00735 GPa @Temperature 110 °C |
1.07 ksi @Temperature 230 °F |
||
| 0.00883 GPa @Temperature 1500 °C |
1.28 ksi @Temperature 2730 °F |
||
| Compressive Strength | 29.4 MPa @Temperature 1100 °C |
4270 psi @Temperature 2010 °F |
Cold Crushing |
| 39.2 MPa @Temperature 110 °C |
5690 psi @Temperature 230 °F |
Cold Crushing | |
| 68.6 MPa @Temperature 1500 °C |
9960 psi @Temperature 2730 °F |
Cold Crushing | |
| 19.6 MPa @Time 86400 sec |
2840 psi @Time 24.0 hour |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.16 W/m-K @Temperature 400 °C, Time 10800 sec |
8.05 BTU-in/hr-ft²-°F @Temperature 752 °F, Time 3.00 hour |
|
| 1.34 W/m-K @Temperature 600 °C, Time 10800 sec |
9.30 BTU-in/hr-ft²-°F @Temperature 1110 °F, Time 3.00 hour |
||
| 1.39 W/m-K @Temperature 800 °C, Time 10800 sec |
9.65 BTU-in/hr-ft²-°F @Temperature 1470 °F, Time 3.00 hour |
||
| Maximum Service Temperature, Air | 1850 °C | 3360 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | >= 96 % | >= 96 % | |
| Fe2O3 | <= 0.30 % | <= 0.30 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | <-0.05 | 800°C |
| <-0.08 | 1100°C | |
| <-0.2 | 1500°C | |
| Refractoriness | <1900°C | |
| Thermal Expansion | 0.9 | Reversible |
| Water Required to Mix | 8-10% |
Users viewing this material also viewed the following:
- FloMet 316L Stainless Steel
- LTL Color Compounds ColorFast® PBT100 PBT
- Lanxess Durethan® BKV 215 H2.0 901510 Copolyamide, 15% Glass Fiber
- Eurostar Staramide RF004EU PA66/6, 20% Glass Fiber Filled, Injection Molded
- Eurostar Starflam PF0023E PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- Dow Corning 1-6136 ANTISTAT
- Bhansali Engineering Abstron SE-32M ABS Sheet Extrusion Grade
- 3M CN-4490 EMI Shielding Tape
Copyright © lookpolymers.com All Rights Reserved