Aclo Accutech Polypropylene Copolymer CP0436W10L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436W10L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 61 | 61 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.350 GPa | 195.8 ksi | ASTM D638 |
| Flexural Strength | 24.0 MPa | 3480 psi | ASTM D790 |
| Flexural Modulus | 1.100 GPa | 159.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm | 2.20 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.8 °C | 127 °F |
Users viewing this material also viewed the following:
- Resin Technology Group EN 139-2 UV Gellable, Low Temperature Cure, One-Component Epoxy Adhesive
- Abatron AboWeld 8012-4/AboCure 8012-4 Epoxy (discontinued **)
- Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, As Conditioned
- Teknor Apex APEX® 90-P513A-75-NT Polyvinyl Chloride+PUR
- UBE UBEPOL BR130B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 35 Minutes at 145°C)
- Borealis BS2581 High Density Polyethylene for Blow Molding
- Eastman Eastman 1223 Copolyester
- Chosun Refractories INCT135S Light-Weight Castable
- Chosun Refractories KSB-AM Special Casting Block
- Arlon 75400R045 0.045" (1.14 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved