Sibur SKI-3 1st Grade, 2nd Group Isoprene Rubber (IR)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Sibur |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sibur SKI-3 1st Grade, 2nd Group Isoprene Rubber (IR).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. For production of tires and rubber technical articles of wide assortment.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 65 - 74 @Temperature 100 °C |
65 - 74 @Temperature 212 °F |
ML 1-4 |
| Ash | <= 0.50 % | <= 0.50 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 28.4 MPa | >= 4120 psi | |
| Tensile Strength, Ultimate | >= 19.6 MPa @Temperature 100 °C |
>= 2840 psi @Temperature 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Loss During Drying | <0.6% | |
| Mass Share of Anti-oxidants | 0.2-0.3% | |
| Mass Share VTS-60 | 0.35-0.55% | |
| Spread Flow Batch Error | <±8 % |
Users viewing this material also viewed the following:
- LG Chemical Lupox® GP-2301F General Purpose PBT, 30% Glass Fiber Reinforced, Flame Retardant
- Mitsui Arlenâ„¢ A315 15% Glass Fiber-Reinforced Modified Nylon 6T (DAM)
- Techmer ES Electrafil® J-3/CF/30 Nylon 6, 30% Carbon Fiber Reinforced
- Shin-Etsu Silicones KE-5560U Low Temperature Silicone Elastomer
- Saint-Gobain COHRlastic® 100S Silicone Sponge/High Temp Silicone Adhesive Pressure Sensitive Tape
- DuPont™ Bynel® 41E871 Anhydride Modified LLDPE
- Ensinger TECAFINE™ PP Polypropylene (PP)
- Fainplast Compounds CKL 66 Flexible PVC, Sheathing Lead Free
- Braskem Green PE SLH218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved