Aclo Accutech Nylon 6 NY0730G30L Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Nylon 6 NY0730G30L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 143.0 MPa | 20740 psi | ASTM D638 |
| Tensile Strength, Yield | 144.0 MPa | 20880 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 4.200 GPa | 609.1 ksi | ASTM D638 |
| Flexural Strength | 213.9 MPa | 31030 psi | ASTM D790 |
| Flexural Modulus | 8.3985 GPa | 1218.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F |
Users viewing this material also viewed the following:
- Indium Corp. 4N Commercial Indium Metal
- Westlake EMAC® Plus SP1358 21.5% Ethylene-Methyl Acrylate Copolymer
- A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene
- Cosmic Plastics E4920 Mineral Filled Epoxy Molding Compound, Encapsulated Grade
- Covestro Desmopan® DP 9650DU Polyurethane
- BASF Ultramid® 8232G HS FR BK-102 25% Glass Filled PA6 (Dry)
- 3M Dyneon™ FX 5929 Polymer Processing Additive
Copyright © lookpolymers.com All Rights Reserved