A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm @Thickness 3.175 mm |
0.0050 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 129.88 MPa | 18837 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 169.84 MPa | 24633 psi | ASTM D790 |
| Flexural Modulus | 8.9915 GPa | 1304.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.81 J/cm | 9.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- DuPont Nucrel® 1302 Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film (discontinued **)
- TSE Industries Millathane® 28 Millable Polyester Polyurethane Rubber
- Ravago Manufacturing Americas Hylon® N1033TL Nylon 6/6 (Cond) (discontinued **)
- JPJ Technologies 700F HDPE Extrusion
- SABIC Innovative Plastics Valox® 310SE0 PBT
- Solvay Specialty Polymers Ryton® R-4-200NA Polyphenylene Sulfide (PPS), 40% Glass Fiber
- Solvay TECHNYL® A 218 MZ15 V 25 PA66, 25/15% glass/mineral fiber, DRY
- Eurotec® Tecomid® NB40 GR25 NL PA 6 25% glass fiber reinforced
- BASF Ultramid® B3Z BK 30464 PA6 (Dry)
- Lehmann & Voss LUVOCOM® 1105-7096 PEEK, with carbon fiber, easy flowing
Copyright © lookpolymers.com All Rights Reserved