- SABIC Innovative Plastics LNP THERMOCOMP EC006E PEI
SABIC Innovative Plastics LNP THERMOCOMP EC006E PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EC006E PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* EC006E is a compound based on Polyetherimide resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| 1.394 g/cc | 0.05036 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0051 cm/cm @Time 86400 sec |
0.0051 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 215 MPa | 31200 psi | ISO 527 |
| 230 MPa | 33400 psi | ASTM D638 | |
| Elongation at Break | 1.3 % | 1.3 % | ISO 527 |
| 1.5 % | 1.5 % | ASTM D638 | |
| Tensile Modulus | 18.47 GPa | 2679 ksi | 1 mm/min; ISO 527 |
| 23.3 GPa | 3380 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 306 MPa | 44400 psi | ISO 178 |
| 314 MPa | 45500 psi | ASTM D790 | |
| Flexural Modulus | 19.16 GPa | 2779 ksi | ASTM D790 |
| 20.8 GPa | 3020 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.52 | 0.52 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.48 | 0.48 | ASTM D3702 Modified |
| K (wear) Factor | 151 x 10-8 mm³/N-M | 75.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 706C (IG) Synthetic Oil
- Polykemi AB POLYfill PPC T10030 Polypropylene Copolymer, Mineral Reinforced
- Petroquimica Triunfo Trithene® TS 7045 LDPE - Film - Plastification
- LyondellBasell Petrothene® NA143063 Low Density Polyethylene
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 65-HR-1 TPE
- Stir SpA AF 95 CZ (PVC)
- Teknor Apex Vidux® CV-1000-76 Polyvinyl Chloride, Flexible
- Braskem Green PE SLH118 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
- BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Conditioned)
- Total Lacqrene® 6630 Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved