Lehmann & Voss LUVOCOM® 20-0659 Polyphthalamide, with carbon fiber
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 20-0659 Polyphthalamide, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Low influence from moisture and temperature to measures and electrical properties, compared with PA66Suitable for metall inserts.Improved friction and wear behaviour. Emergency running property.Bearings, sleeves, sliding elements, control disks, gear wheels, duty parts in switches.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 275 MPa | 39900 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.0 % | 2.0 % | flexural | |
| Modulus of Elasticity | 25.0 GPa | 3630 ksi | |
| Flexural Strength | 360 MPa | 52200 psi | |
| Flexural Modulus | 23.0 GPa | 3340 ksi | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | edgewise; ISO 179 1eU |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.0 µm/m-°C | 7.22 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.480 W/m-K | 3.33 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| 195 °C | 383 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 100 ohm | <= 100 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 320 - 330 °C | 608 - 626 °F | |
| Zone 1 | 320 - 340 °C | 608 - 644 °F | |
| Zone 2 | 320 - 345 °C | 608 - 653 °F | |
| Zone 3 | 325 - 350 °C | 617 - 662 °F | |
| Mold Temperature | 135 - 160 °C | 275 - 320 °F | |
| Drying Temperature | 80.0 °C @Time 57600 sec |
176 °F @Time 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 18000 sec |
221 °F @Time 4.00 - 5.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- NOVA Chemicals Dylark® FG7300 High-Heat Styrenic Copolymer
- ExxonMobil ESCOR™ AT 320 Cast Film Resin (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP UX06425 PPA
- Techmer ES HiFill® PA6 GF/M40 IG BK 40% Glass/Mineral Filled
- Master Bond SteelMaster 43HT Stainless Steel Filled Two Component Epoxy System
- Covestro Makroblend® DP UT3905 Polycarbonate + PBT, Impact Grade
- BNZ Materials Marinite® C Ceramic Board for Aluminum Contact
- Bohler-Uddeholm UDDEHOLM VANADIS 23 (AISI M3:2) Hot Work Tool Steel
- Ashley Polymers Ashlene® R190B Acetal
Copyright © lookpolymers.com All Rights Reserved