- Aremco Ceramabond™ 885 High Temperature Ceramic Adhesive/Paste, Zirconia Filled
Aremco Ceramabond™ 885 High Temperature Ceramic Adhesive/Paste, Zirconia Filled
| Category | Ceramic , Oxide , Zirconium Oxide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 885 High Temperature Ceramic Adhesive/Paste, Zirconia Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: Fiber-Reinforced, Sets @ RT Bonding: Ceramic to Ceramic, Ceramic to Metal Principal Use: Halogen Lamps
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.65 - 2.70 g/cc | 0.0957 - 0.0975 lb/in³ | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 10000 - 20000 cP | 10000 - 20000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 54.2 J | 40.0 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.20 µm/m-°C | 4.00 µin/in-°F | |
| Maximum Service Temperature, Air | 1760 °C | 3200 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 4.13 kV/mm | 105 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
Step 1, preceeded by <1 hour air set |
| 120 min @Temperature 260 °C |
2.00 hour @Temperature 500 °F |
Step 2 | |
| 120 min @Temperature 371 °C |
2.00 hour @Temperature 700 °F |
Step 3 | |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | after curing at 700°F for 2 hours |
| Alkali Resistance | Good | after curing at 700°F for 2 hours |
| Color | Tan | |
| Moisture Resistance | Good | after curing at 700°F for 2 hours |
| Solvent | Water | |
| Thinner | 885-T |
Users viewing this material also viewed the following:
- LG Chemical Lupox® PBT-GP-2156F 15% GFR Flame Retardant PBT
- Lubriplate 930-A Bentone Type Multi-Purpose Grease
- Lucent Polymers GPP-130 Polypropylene Homopolymer, 30% Glass Fiber Reinforced, Chemically Coupled
- Williams Advanced Alloys WS174 Solder
- Hippe PF CC 33 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod
- Dow Corning Z-6042 SILANE
- Dymax 630 Structural Adhesive
- Asahi Kasei Thermylon® NSG-730A 65% Ceramic and Glass Fiber Reinforced
- BASF Novolen® 1104 K Polypropylene
- ChevronTexaco Rando® HD 32 Ashless
Copyright © lookpolymers.com All Rights Reserved