Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Strength | 50.0 kV/mm @Thickness 0.533 mm, Temperature 23.0 °C |
1270 kV/in @Thickness 0.0210 in, Temperature 73.4 °F |
50% RH, ASTM D149-97a(04); ASTM D149 |
PolyOne OnFlex™ HFFR 310-01 Thermoplastic Elastomer (TPE) OnFlex™ HFFR 310-01 is a non-halogen flame retardant material designed for cable jackets. New Product. Commercial specifications have not been established. - Non-halogen flame retardant - UL62 comp.. |
|||
Dielectric Strength | 50.0 kV/mm @Thickness 0.533 mm, Temperature 23.0 °C |
1270 kV/in @Thickness 0.0210 in, Temperature 73.4 °F |
50% RH, ASTM D149-97a(04); ASTM D149 |
PolyOne OnFlex™ HFFR 320-01 Thermoplastic Elastomer (TPE) OnFlex™ HFFR 320-01 is a non-halogen flame retardant material designed for flexible power cord insulation and cable jackets. New Product. Commercial specifications have not been established. - Non-.. |
|||
Dielectric Strength | >= 50.0 kV/mm | >= 1270 kV/in | ISO.243 DN.53481 |
Polimersan Plastics POLIPOLEN® (Polyethylene) HD-PE 300 PE 300: Polyethylene with high density. POLIPOLEN® PE (POLYETHYLENE) is maintained from coke oven gas or from natural gas or from Ethene or Ethane which is produced by cracking of petroleum. Monom.. |
|||
Dielectric Strength | >= 50.0 kV/mm | >= 1270 kV/in | ISO.243 DN.53481 |
Polimersan Plastics POLIPOLEN® (Polyethylene) HD-PE 500 PE 500: Polyethylenes with molecular weight higher than 500,000 gr/mol. POLIPOLEN® PE (POLYETHYLENE) is maintained from coke oven gas or from natural gas or from Ethene or Ethane which is produce.. |
|||
Dielectric Strength | 50.0 - 80.0 kV/mm | 1270 - 2030 kV/in | ASTM D149; ISO.243 DN.53481 |
Polimersan Plastics POLITEF® (PTFE) POLITEF (PTFE) was invented in 1938. It is the most preferable and known fluoropolymer among fluorine polymers. It has superior properties that none of the other industrial plastics have because of .. |
|||
Dielectric Strength | 50.0 - 80.0 kV/mm | 1270 - 2030 kV/in | ASTM D149; ISO.243 DN.53481 |
Polimersan Plastics POLITEF® (PTFE) POLITEF (PTFE) was invented in 1938. It is the most preferable and known fluoropolymer among fluorine polymers. It has superior properties that none of the other industrial plastics have because of .. |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | Step by step |
Natural Rubber, Vulcanized (NR, IR, Polyisoprene) Natural rubber is polyisoprene. Chemical and environmental resistance and mechanical properties are improved through crosslinking (vulcanizing), usually through treatment with sulfur.Natural rubber.. |
|||
Dielectric Strength | 50.0 - 80.0 kV/mm @Thickness 0.200 mm |
1270 - 2030 kV/in @Thickness 0.00787 in |
VDE 0303 Part 2 |
Fluorseals PTFE Unfilled Information provided by TEKU GmbH Fluorkunststoffe, a distributor of Fluorseals materials. |
|||
Dielectric Strength | 50.0 - 80.0 kV/mm | 1270 - 2030 kV/in | DIN 53481 |
Isoflon ECTFE Fluoropolymer Fluoropolymer material specifications.Information provided by Isoflon. |
|||
Dielectric Strength | 50.0 - 80.0 kV/mm | 1270 - 2030 kV/in | DIN 53481 |
Isoflon PFA Polyperfluoroalkoxyethylene Fluoropolymer material specifications.Information provided by Isoflon. |
|||
Dielectric Strength | 50.0 - 90.0 kV/mm | 1270 - 2290 kV/in | DIN 53481 |
Isoflon PEHD 300 High Density Polyethylene Products with excellent friction, anti-stick, abrasion and chemical inertia characteristicsVery good impact resistanceNo moisture regainProduct for the food industryInformation provided by Isoflon. |
|||
Dielectric Strength | >= 50.0 kV/mm | >= 1270 kV/in | Transformer Oil; Ø 93x3mm; IEC 243-1 |
SYNTHOS Krasten® 154 General Purpose Polystyrene Improved heat resistance, very good rheological properties.Examples of Application:Injection moulding – dishes, jars, Petri dishes, screw caps.Extrusion – blends with high impact polystyre.. |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
Schwartz Technical Plastics LAMIGAMID® 200 Polyamide 66, Dry Application: bearing bushes, machine parts, gears, linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
Schwartz Technical Plastics LAMIGAMID® 307 Cast Polyamide 6, Heat Stabilized, Dry Application: slippers, inserts for coupling boxesInformation provided by Schwartz Technical Plastics GmbH |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
Schwartz Technical Plastics LAMIGAMID® 309 Cast Polyamide 6, Oil Filled, Dry Application: slippers, inserts for coupling boxes, wear linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
Schwartz Technical Plastics LAMIGAMID® 314 Cast Polyamide 6, MoS2 Filled, Heat Stabilized, Dry Application: sheaves, wheels, gear-rods, gears, sliding linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
Schwartz Technical Plastics LAMIGAMID® 327 Cast Polyamide 6, MoS2, Heat Stabilized, Dry Application: heavy-duty wheels, running speed up to 3m/sInformation provided by Schwartz Technical Plastics GmbH |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
Schwartz Technical Plastics LAMIGAMID® 710 High Density Polyethylene Application: chain-guides, cutting plates, linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
Zell-Metall Engineering Plastics Zellamid 1200 G at 50% RH Zellamid® 1200 G is manufactured by an activated anionic reaction. Finished and semi-finished parts are produced by a static cast process. This process makes it possible to produce a material wit.. |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | IEC 243; DIN 53481 |
Zell-Metall Engineering Plastics Zellamid 1400 (PET) Zellamid® 1400 is the registered trademark of Zell-Metalls partly crystalline thermoplastic Polyester based on Polyethylene Terephthalate.This PETP features outstanding dimensional stability, .. |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | Short Time, 500V/sec; ASTM D149 |
Eastman Sahara Film Sahara Films are developed for use in applications where increased temperature resistance is desired.Applications/UsesHigh temperature printable films |
|||
Dielectric Strength | 50.0 kV/mm @Thickness 1.00 mm |
1270 kV/in @Thickness 0.0394 in |
ASTM D877 |
ChevronTexaco Transformer Oil Texaco Transformer Oil and Texaco Transformer Oil Inhibited deliver value through:Prolonged transformer life — Excellent conductive heat transfer properties improve cooling of transformer component.. |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | |
Arkema Group Cristamid® MS 1700 Semi-Aromatic Nylon (PASA) (Conditioned) Designation ISO 1874-PA12/xx,M,12-020Semi-aromatic polyamide (PASA) grade for injection molding.Transparency even thick. Outstanding thermal properties due to its high glass temperature. Good chemic.. |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | |
Arkema Group Cristamid® MS 1300 Semi-Aromatic Nylon (PASA) (Conditioned) Designation ISO 1874-PA12/xx,MR,12-020Semi-aromatic polyamide (PASA) grade for injection molding and tubes extrusion.Transparency even thick. High resistance to environmental stress cracking. Good t.. |
|||
Dielectric Strength | 50.0 kV/mm | 1270 kV/in | ASTM D149 |
Solvay Specialty Polymers Algoflon® A.30 PTFE (Polytetrafluoroethylene)
(discontinued **) Data provided by the manufacturer.Type IV.G.2 (except elongation at break) Classification. Suspension polymer powder grade recommended for compression molding and extrusion. PTFE possesses high iner.. |