Schwartz Technical Plastics LAMIGAMID® 710 High Density Polyethylene
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Cast |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 710 High Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: chain-guides, cutting plates, linersInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.955 g/cc | 0.0345 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 0.00 % | 0.00 % | DIN 53473 |
| Water Absorption at Saturation | >= 0.10 % @Temperature 20.0 °C |
>= 0.10 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 36.0 MPa | 5220 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO-DIS 527 |
| Creep Strength | 2.80 MPa | 406 psi | 1% elongation, 1000 h; DIN 53444 |
| 4.50 MPa | 653 psi | 2% elongation, 1000 h; DIN 53444 | |
| Tensile Modulus | 1.00 GPa | 145 ksi | DIN 53457 |
| Flexural Strength | 31.0 MPa | 4500 psi | DIN 54352 |
| Flexural Modulus | 0.900 GPa | 131 ksi | DIN 53457 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | DIN 53453 |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.020 - 0.080 | 0.020 - 0.080 | With lubrication |
| Coefficient of Friction, Dynamic | 0.29 | 0.29 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | >= 8.0 | >= 8.0 | ISO-DIS 527 |
| K Factor (Wear Factor) | 1.0e-9 | 1.0e-9 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 200 µm/m-°C @Temperature 20.0 - 100 °C |
111 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 2.30 J/g-°C | 0.550 BTU/lb-°F | |
| Thermal Conductivity | 0.140 W/m-K | 0.972 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 130 °C | 266 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous |
| 120 °C | 248 °F | Intermittent | |
| Minimum Service Temperature, Air | -100 °C | -148 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.3 | 3.3 | DIN 53483 |
| Dielectric Strength | 50.0 kV/mm | 1270 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.00020 | 0.00020 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA3b | DIN 53480 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging 161J1-3V Polyvinyl Chloride, Rigid (PVC, Rigid)
- MV Labs TB500 TbF3 Terbium fluoride
- Orion Engineered Carbons ECORAX® S 204 Carbon Black
- Plastcom SLOVALEN PC 93 T 20 PP, 20% mineral filling, UV stabilization
- Indium Corp. Indalloy 176 Zinc Solder Alloy
- Schott N-LAF36 Glass
- SMAC SMACMOUNT® 2528S 01 Damping Material
- Denka VINYKON R2001 PVC, R grade for hard extrusion
- ATI Allegheny Ludlum AL 15-5 High Strength Stainless Steel, UNS S15500
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 6.0 PHR MBTS
Copyright © lookpolymers.com All Rights Reserved