Polymer Property : Cure Time = 1.00 hour Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Cure Time	40.0 - 60.0 min	0.667 - 1.00 hour	working strength
Permabond TA430 Acrylic Adhesive & Initiator PERMABOND TA430 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics, wood, and some thermoplastics. This adhesive may be used in a variety of structural bondin..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	working strength
Permabond TA435 Toughened Acrylic Adhesive & Initiator PERMABOND TA435 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some thermoplastics. This adhesive may be used in a variety of structural bonding appli..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	working strength
Permabond TA436 Toughened Acrylic Adhesive PERMABOND TA436 is a structural acrylic adhesive designed primarily for bonding metals, ferrites, ceramics and some thermoplastics. Permabond TA436 is a no-mix system which obtains handling strength..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	working strength
Permabond TA437 Toughened Acrylic Adhesive PERMABOND TA437 is a single component structural acrylic adhesive designed primarily for bonding metals, ferrites and ceramics. The typical fixture time of TA437 when used with Initiator 41 is 30 –..
Cure Time	3.00 - 60.0 min @Temperature 60.0 - 170 °C	0.0500 - 1.00 hour @Temperature 140 - 338 °F	Average value: 25.8 min Grade Count:12
Overview of materials for Cyanoacrylate Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Cyanoacrylate Adhesive". Each property range of values reported is minimum and maximum values of appropr..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	Ambient
Reltek BONDiT™ A-43 Bonding Agent, Primer and Adhesive Key Properties: Adhesion promoter for most thermoplastics, thermoset materials, elastomers, polyurethanes.Can be used on metals, glass and ceramicApplications: High functionality produces good bond ..
Cure Time	45.0 - 60.0 min @Temperature 60.0 Â°C	0.750 - 1.00 hour @Temperature 140 Â°F	Full cure in 45 to 60 mins at 140Â°F.
Fibre Glast 1101 High-Strength General Purpose Epoxy Adhesive Description:#1101 is a light grayish-tan two part epoxy adhesive that was developed especially for difficult bonding problems involving similar or dissimilar materials. #1101 provides excellent adhe..
Cure Time	45.0 - 60.0 min	0.750 - 1.00 hour	Functional cure
ITW Devcon 5 minuteÂ® Epoxy, Light Amber Information provided by ITW Devcon
Cure Time	30.0 - 60.0 min @Temperature 150 Â°C	0.500 - 1.00 hour @Temperature 302 Â°F
Gwent Electronic Materials C2050425D1 Curable Carbon Ink This product is based on a unique curing process that results in the low temperature formation of a thermosetting conductive coating that combines good adhesion with excellent chemical, solvent and ..
Cure Time	30.0 - 60.0 min @Temperature 120 Â°C	0.500 - 1.00 hour @Temperature 248 Â°F
Gwent Electronic Materials C2050503D1 Curable Carbon Ink This product is based on a unique curing process that results in the low temperature formation of a thermosetting conductive coating that combines good adhesion with excellent chemical, solvent and ..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour
Trelleborg Emerson & Cuming Stycast® 1090/11 Two-Component General Purpose Encapsulant Features and Typical Applications: Designed as general purpose encapsulants, these products offer a wide range of features including thermal conductivity, mechanical shock and impact resistance, as ..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour
Trelleborg Emerson & Cuming Stycast® 2057FR/11 Two-Component Epoxy Flame Retardant Encapsulant Features and Typical ApplicationsProvide flame resistance down to 1/8 of an inch. These products also offer various other features such as thermal shock protection, low viscosity, and thermal conduc..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour
Trelleborg Emerson & Cuming Stycast® 2651-40FR/9 Two-Component Epoxy Flame Retardant Encapsulant Features and Typical ApplicationsProvide flame resistance down to 1/8 of an inch. These products also offer various other features such as thermal shock protection, low viscosity, and thermal conduc..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour
Trelleborg Emerson & Cuming Stycast® 2850FT-FR/11 Two-Component Epoxy Flame Retardant Encapsulant Features and Typical ApplicationsProvide flame resistance down to 1/8 of an inch. These products also offer various other features such as thermal shock protection, low viscosity, and thermal conduc..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	Dry to touch, RT @ 50%RH
3M CP 25WB+ Fire Barrier Sealant 3M Fire Barrier Sealant CP 25WB+ is a high-performance, ready-to-use, gun-grade, latex-based, intumescent sealant that dries to form a monolithic fire-stop seal that also acts as a barrier to airbor..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	Dry to touch, RT @ 50%RH
3M IC 15WB+ Fire Barrier Sealant 3M Fire Barrier Sealant IC 15WB+ is a cost-effective, one-part, gun-grade, latex-based, intumescent firestop sealant that dries to form a monolithic firestop seal that also acts as a barrier to airb..
Cure Time	45.0 - 60.0 min	0.750 - 1.00 hour	Tack Free Time, catalyzed with QM CAT RED 3
ACC QM 107 QSI Quantum Silicones 7 Durometer Condensation Cure Moldmaking Material QM 107 is a two component, room temperature condensation cure silicone material. The cured rubber is very soft, has excellent mechanical properties and good shelf-life stability. This material is us..
Cure Time	45.0 - 60.0 min	0.750 - 1.00 hour	Tack Free Time, catalyzed with QM CAT RED 3
ACC QM 122 QSI Quantum Silicones 22 Durometer Condensation Cured Moldmaking Material QM 122 is a two-component, room temperature condensation cure silicone material. The cured rubber is flexible with excellent mechanical and physical properties in addition to good shelf-life stabili..
Cure Time	20.0 - 60.0 min @Temperature 24.0 °C	0.333 - 1.00 hour @Temperature 75.2 °F
BCC Products BC 4544 Polyester Carvable Wood Filler This polyester resin base compound is easy to use, sets in minutes and can be sanded or carved almost immediately. Acts like wood yet exhibits no grain problems. BC4544 Wood Filler can be carved, sa..
Cure Time	20.0 - 60.0 min @Temperature 24.0 °C	0.333 - 1.00 hour @Temperature 75.2 °F
BCC Products BC 4553 Polyester Styling Paste BC4553 is designed for instant buildup and repair of plastic surfaces and models. Recommended for use on SMC and FRP parts, vacuum form molds and a variety of surfaces. When cured BC4553 produces a ..
Cure Time	45.0 - 60.0 min	0.750 - 1.00 hour	Touch Dry
3M Scotchkote™ XF 895 Fast Curing Floor Coating Scotchkote Fast Curing Floor Coating XF 895 has been specifically developed as a high build floor protection system for application to concrete surfaces, to provide rapid return to serviceProduct Fe..
Cure Time	30.0 - 60.0 min @Temperature 25.0 °C	0.500 - 1.00 hour @Temperature 77.0 °F	demold time
BCC Products DP-11-90 Urethane Casting DP-11-90 is an unfilled, low viscosity, quick setting two component urethane system. An easy to use 1 to 1 mix ratio (Part A/Part B), DP-11-90 offers the user a 3 minute working time with parts demo..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	Air Set prior to curing
Aremco Aremco-Seal™ 529VHV High Temperature Specialty Coatings Silicone Very high viscosity version, transparent silicone sealer with exceptional electrical and moisture resistance to 600°F (316°C). Ideal for use in cartridge heaters.
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	at 200°F; 0.75-1 hr at 480°F
Aremco Aremco-Seal™ 529VHV High Temperature Specialty Coatings Silicone Very high viscosity version, transparent silicone sealer with exceptional electrical and moisture resistance to 600°F (316°C). Ideal for use in cartridge heaters.
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	Air Set prior to curing
Aremco Aremco-Seal™ 613 High Temperature Specialty Coatings Glass
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	Dry to touch, RT @ 50%RH
3M FD 150+ Fire Barrier Sealant 3M Fire Barrier Sealant FD 150+ is an economical, ready to use, gun-grade, elastomeric sealant that dries to from a monolithic flexible firestop seal. 3M Fire Barrier Sealant FD 150+ firestops joint..
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	at 200°F; 0.75-1 hr at 480°F
Aremco Aremco-Seal™ 529HV High Temperature Specialty Coatings Silicone High viscosity version, transparent silicone sealer with exceptional electrical and moisture resistance to 600°F (316°C). Ideal for use in cartridge heaters.
Cure Time	30.0 - 60.0 min	0.500 - 1.00 hour	Dry to touch, RT @ 50%RH
3M 1003 SL Fire Barrier Water Tight Sealants 3M Fire Barrier Water Tight Sealants 1000 NS and 1003 SL are ready-to-use, single component, neutral cure, silicone sealants that cure upon exposure to atmospheric humidity to form a flexible firest..
Cure Time	40.0 - 60.0 min	0.667 - 1.00 hour	handling time
Permabond ET514 Epoxy Resin PERMABOND ET514 is a 1:1 mixable epoxy adhesive. It has excellent resistance to impact and vibration and is ideal for structural bonding of metal, wood, composites and certain plastics. Its rapid cu..