- Polymer Property : Thermal Conductivity = 201 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 201 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 29.0 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Outokumpu 153MA™ High Temperature Austenitic Stainless Steel Variant of 1.4301 with increased silicon and nitrogen contents and microalloyed with rare earth metals (REM). This raises the max service temperature in dry air to 1000°C.Applications: Heat and cr.. |
|||
| Thermal Conductivity | 29.0 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Outokumpu 253MA® High Temperature Austenitic Stainless Steel Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used be.. |
|||
| Thermal Conductivity | 29.0 W/m-K @Temperature 85.0 °C |
201 BTU-in/hr-ft²-°F @Temperature 185 °F |
|
| Indium Corp. Indalloy® 205 In-Pb Solder Alloy Indalloy's #7, #10, #150, #204, #205 and #206 comprise a group of lead-indium solders designed to cover the temperature range of 165°C-275°C. All have the minimum gold-leaching characteristics.. |
|||
| Thermal Conductivity | 29.0 W/m-K @Temperature 20.0 °C |
201 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| Industeel CLC 1.2738 Prehardened Mold Steel (300HB/30HRC) for Thick Sections Description: CLC 1.2738 is a 300HB (30HRC) pre-hardened grade specially designed for plastic mold industry. Chromium, Molybdenum, Nickel carbon and manganese additions are optimized to have a fully .. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 29.0 W/m-K | 201 BTU-in/hr-ft²-°F | |
| Williams Advanced Alloys WS185 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
| Thermal Conductivity | 29.0 W/m-K | 201 BTU-in/hr-ft²-°F | |
| Williams Advanced Alloys WS226 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
| Thermal Conductivity | 28.9 W/m-K | 201 BTU-in/hr-ft²-°F | |
| California Fine Wire Nickel Alloy 120 Nickel Iron Resistance Wire All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
| Thermal Conductivity | 29.0 W/m-K @Temperature 20.0 - 100 °C |
201 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
|
| Anderman Ceramics EA999 Sintered Alumina, 99.9% Densely sintered alumina is characterized by: high strength and hardness, temperature stability, electrical insulation, and high wear resistance and corrosion resistance even at high temperatures. .. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||