Industeel CLC 1.2738 Prehardened Mold Steel (300HB/30HRC) for Thick Sections
| Category | Metal , Ferrous Metal , Carbon Steel , High Carbon Steel , Tool Steel , Mold Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | CLC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel CLC 1.2738 Prehardened Mold Steel (300HB/30HRC) for Thick Sections.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: CLC 1.2738 is a 300HB (30HRC) pre-hardened grade specially designed for plastic mold industry. Chromium, Molybdenum, Nickel carbon and manganese additions are optimized to have a fully martensite-bainite microstructure after quenching. The high nickel content (1%) is specially adapted to ensure a perfect homogeneity of structure and hardness through thickness even for very thick blocks (up to 700mm/28"). The steel is melted in electrical furnace and refined with VOD or DH device The cleanliness of the steel is guaranteed as well as the soundness. This makes the steel particularly well adapted for mold even when polishing or chemical etching are required for surface finish quality.Information provided by manufacturer.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 300 | 300 | Typical, in Transverse Direction |
| Tensile Strength, Ultimate | 993 MPa | 144000 psi | Typical, Transverse Direction |
| Tensile Strength, Yield | 826 MPa @Strain 0.200 % |
120000 psi @Strain 0.200 % |
Typical, Transverse Direction |
| Elongation at Break | 17 % | 17 % | Typical, EL 5.65 Transverse Direction |
| Modulus of Elasticity | 205 GPa | 29700 ksi | Typical, in Transverse Direction |
| Charpy Impact | 22.0 J | 16.2 ft-lb | Typical (Transverse) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.7 µm/m-°C @Temperature 20.0 - 200 °C |
7.06 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Thermal Conductivity | 29.0 W/m-K @Temperature 20.0 °C |
201 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.40 % | 0.40 % | |
| Chromium, Cr | 1.9 % | 1.9 % | |
| Iron, Fe | 94.683 - 94.7 % | 94.683 - 94.7 % | As remainder |
| Manganese, Mn | 1.5 % | 1.5 % | |
| Molybdenum, Mo | 0.20 % | 0.20 % | |
| Nickel, Ni | 1.0 % | 1.0 % | |
| Phosphorous, P | <= 0.012 % | <= 0.012 % | |
| Silicon, Si | 0.30 % | 0.30 % | |
| Sulfur, S | <= 0.0050 % | <= 0.0050 % |
Users viewing this material also viewed the following:
- P & P Technology CB 70 Carbon Loaded Silicone
- STAR Thermoplastic Alloys & Rubbers StarMediflex P 7020-1000 TPE
- SMAC SMACMOUNT® 2528S Damping Material
- Tisan TISOPLEN® 40% Calcite Filled Heat Stabilized Homopolymer Polypropylene
- Plenco 3597 Phenolic, Granular, Injection Molded
- ExxonMobil LD 200.48 Extrusion Coating and Laminating Resin
- Eurostar Staramide AG7K PA66, 35% Glass Filled, Injection Molded
- Adamas Adalon® 812 PTFE, 46% Bronze, Green
- Beijing Ranger Chem SM-601 Solid Epoxy Resin
- Atom Adhesives AA-DUCT 906 Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved