Category | Metal , Superalloy , Iron Base |
Manufacturer | Haynes International, Inc. |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 8.23 g/cc | 0.297 lb/in³ | at RT |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 860 MPa | 125000 psi | |
Tensile Strength, Yield | 460 MPa @Strain 0.200 % |
66700 psi @Strain 0.200 % |
|
Elongation at Break | 42.4 % | 42.4 % | in 50.8 mm |
Modulus of Elasticity | 205 GPa | 29700 ksi | RT |
138 GPa @Temperature 1000 °C |
20000 ksi @Temperature 1830 °F |
||
143 GPa @Temperature 900 °C |
20700 ksi @Temperature 1650 °F |
||
148 GPa @Temperature 800 °C |
21500 ksi @Temperature 1470 °F |
||
155 GPa @Temperature 700 °C |
22500 ksi @Temperature 1290 °F |
||
164 GPa @Temperature 600 °C |
23800 ksi @Temperature 1110 °F |
||
172 GPa @Temperature 500 °C |
24900 ksi @Temperature 932 °F |
||
179 GPa @Temperature 400 °C |
26000 ksi @Temperature 752 °F |
||
187 GPa @Temperature 300 °C |
27100 ksi @Temperature 572 °F |
||
195 GPa @Temperature 200 °C |
28300 ksi @Temperature 392 °F |
||
200 GPa @Temperature 100 °C |
29000 ksi @Temperature 212 °F |
||
Charpy Impact | 240 J | 177 ft-lb | Samples did not break. Average of 4 or more tests. |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 14.7 µm/m-°C @Temperature 25.0 - 100 °C |
8.17 µin/in-°F @Temperature 77.0 - 212 °F |
|
14.9 µm/m-°C @Temperature 25.0 - 200 °C |
8.28 µin/in-°F @Temperature 77.0 - 392 °F |
||
15.1 µm/m-°C @Temperature 25.0 - 300 °C |
8.39 µin/in-°F @Temperature 77.0 - 572 °F |
||
15.4 µm/m-°C @Temperature 25.0 - 400 °C |
8.56 µin/in-°F @Temperature 77.0 - 752 °F |
||
15.7 µm/m-°C @Temperature 25.0 - 500 °C |
8.72 µin/in-°F @Temperature 77.0 - 932 °F |
||
16.1 µm/m-°C @Temperature 25.0 - 600 °C |
8.94 µin/in-°F @Temperature 77.0 - 1110 °F |
||
16.4 µm/m-°C @Temperature 25.0 - 700 °C |
9.11 µin/in-°F @Temperature 77.0 - 1290 °F |
||
16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
||
17.0 µm/m-°C @Temperature 25.0 - 900 °C |
9.44 µin/in-°F @Temperature 77.0 - 1650 °F |
||
17.1 µm/m-°C @Temperature 25.0 - 1000 °C |
9.50 µin/in-°F @Temperature 77.0 - 1830 °F |
||
Specific Heat Capacity | 0.464 J/g-°C | 0.111 BTU/lb-°F | RT |
0.475 J/g-°C @Temperature 100 °C |
0.114 BTU/lb-°F @Temperature 212 °F |
||
0.493 J/g-°C @Temperature 200 °C |
0.118 BTU/lb-°F @Temperature 392 °F |
||
0.508 J/g-°C @Temperature 300 °C |
0.121 BTU/lb-°F @Temperature 572 °F |
||
0.523 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
||
0.538 J/g-°C @Temperature 500 °C |
0.129 BTU/lb-°F @Temperature 932 °F |
||
0.552 J/g-°C @Temperature 600 °C |
0.132 BTU/lb-°F @Temperature 1110 °F |
||
0.561 J/g-°C @Temperature 700 °C |
0.134 BTU/lb-°F @Temperature 1290 °F |
||
0.570 J/g-°C @Temperature 800 °C |
0.136 BTU/lb-°F @Temperature 1470 °F |
||
0.595 J/g-°C @Temperature 900 °C |
0.142 BTU/lb-°F @Temperature 1650 °F |
||
0.618 J/g-°C @Temperature 1000 °C |
0.148 BTU/lb-°F @Temperature 1830 °F |
||
0.638 J/g-°C @Temperature 1100 °C |
0.152 BTU/lb-°F @Temperature 2010 °F |
||
Thermal Conductivity | 11.1 W/m-K | 77.0 BTU-in/hr-ft²-°F | RT |
13.1 W/m-K @Temperature 100 °C |
90.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
||
15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
||
17.3 W/m-K @Temperature 300 °C |
120 BTU-in/hr-ft²-°F @Temperature 572 °F |
||
19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
||
20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
||
22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
||
24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
||
25.5 W/m-K @Temperature 800 °C |
177 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
27.2 W/m-K @Temperature 900 °C |
189 BTU-in/hr-ft²-°F @Temperature 1650 °F |
||
28.9 W/m-K @Temperature 1000 °C |
201 BTU-in/hr-ft²-°F @Temperature 1830 °F |
||
30.4 W/m-K @Temperature 1100 °C |
211 BTU-in/hr-ft²-°F @Temperature 2010 °F |
||
Melting Point | 1330 - 1415 °C | 2430 - 2579 °F | |
Solidus | 1330 °C | 2430 °F | |
Liquidus | 1415 °C | 2579 °F |
Component Elements Properties | Metric | English | Comments |
---|---|---|---|
Aluminum, Al | 0.20 % | 0.20 % |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0000952 ohm-cm | 0.0000952 ohm-cm | RT |
0.0000986 ohm-cm @Temperature 100 °C |
0.0000986 ohm-cm @Temperature 212 °F |
||
0.0001026 ohm-cm @Temperature 200 °C |
0.0001026 ohm-cm @Temperature 392 °F |
||
0.0001065 ohm-cm @Temperature 300 °C |
0.0001065 ohm-cm @Temperature 572 °F |
||
0.0001095 ohm-cm @Temperature 400 °C |
0.0001095 ohm-cm @Temperature 752 °F |
||
0.0001125 ohm-cm @Temperature 500 °C |
0.0001125 ohm-cm @Temperature 932 °F |
||
0.0001151 ohm-cm @Temperature 600 °C |
0.0001151 ohm-cm @Temperature 1110 °F |
||
0.0001172 ohm-cm @Temperature 700 °C |
0.0001172 ohm-cm @Temperature 1290 °F |
||
0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
||
0.0001207 ohm-cm @Temperature 900 °C |
0.0001207 ohm-cm @Temperature 1650 °F |
||
0.0001223 ohm-cm @Temperature 1000 °C |
0.0001223 ohm-cm @Temperature 1830 °F |
||
0.0001237 ohm-cm @Temperature 1100 °C |
0.0001237 ohm-cm @Temperature 2010 °F |