- Polymer Property : CTE, linear = 11.1 µin/in-°F
Polymer Property : CTE, linear = 11.1 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 - 40.0 µm/m-°C @Temperature 50.0 - 150 °C |
11.1 - 22.2 µin/in-°F @Temperature 122 - 302 °F |
ISO 11359-2 |
| Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi.. |
|||
| CTE, linear | 20.0 - 30.0 µm/m-°C @Temperature 50.0 - 100 °C |
11.1 - 16.7 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
| Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow.. |
|||
| CTE, linear | 20.0 - 30.0 µm/m-°C @Temperature 50.0 - 100 °C |
11.1 - 16.7 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
| Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta.. |
|||
| CTE, linear | 20.0 - 40.0 µm/m-°C @Temperature 50.0 - 150 °C |
11.1 - 22.2 µin/in-°F @Temperature 122 - 302 °F |
Average value: 30.0 µm/m-°C Grade Count:2 |
| Overview of materials for Silicone, Molded, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Silicone, Molded, Glass Fiber Filled". Each property range of values reported is minimum and maximum val.. |
|||
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | DIN 53752 |
| Lehmann & Voss LUVOCOM® 3/CF/30/EG Polyamide 6, with carbon fiber, extrusion grade Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.dynamic stressElectrically conductive, suitable.. |
|||
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | Perpendicular (002) |
| Mateck Highly Oriented Pyrolytic Graphite Oxidic single crystals. Applications include:Scanning tunneling microscopy-callibration and substratesGraphite monochromatorsx-ray diffractionneutron scattering and diffraction |
|||
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM D696 |
| Kolon KOPA® KN333G25CRBK G/F Reinforced Nylon 66 EG-resistant, high strength, dimensionally stableApplications Cooling water pipesInformation provided by API-Kolon. |
|||
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM D696 |
| Kolon KOPA® KN333G30BL G/F Reinforced Nylon 66 G/F 30% reinforcedApplications Engine coversInformation provided by API-Kolon. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Kolon KOPA® KN333G33CR G/F Reinforced Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | DIN 53752 |
| Lehmann & Voss LUVOCOM® 1-0784 Polyamide 66, with glass fiber and carbon fiber, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia comp.. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
|
| Indium Corp. Indalloy 1 Indium-Tin Solder Alloy Fair wettability on glass, quartz, and many ceramics. Good low temperature malleability. Compensates for some CTE mismatch. Low vapor pressureInformation Provided by Indium Corporation |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
| A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-2 |
| Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Dry Information provided by Unitika Ltd. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Toyobo VYLOPET® EMC545 Injection Molding Polyester Resin, Glass Reinforced Applications: Auto-partsFeatures: Ultrasonic weldabilityGlass fiber reinforcementInformation provided by Toyobo. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-2 |
| Polyplastics Duranex® 353RA Polybutylene Terephthalate (PBT), Resin adhesion improved for multiple injection molding, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
| CTE, linear | 20.0 - 21.0 µm/m-°C @Temperature 20.0 °C |
11.1 - 11.7 µin/in-°F @Temperature 68.0 °F |
biax film |
| Goodfellow Polyethylene Naphthalate (PEN) Film A polyester that is chemically quite similar to PET but which is more temperature resistant. So far available only as biaxially oriented and heat stabilized films, they are semi-crystalline and colo.. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
| CP-Polymer-Technik Wellamid® 6000 GVS 20/10 HWCP 20% Glass Fiber and 10% Glass Sphere Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
| DSM Stanyl® TW241F6 Nylon 46-30% Glass Reinforced, Heat Stabilized, Lubricated (Asian Grade) (Dry) Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper.. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
| CP-Polymer-Technik Wellamid® 6600 GV 30 HWCP 30% Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
| CTE, linear | 20.0 - 30.0 µm/m-°C | 11.1 - 16.7 µin/in-°F | |
| Hippe PBT GF 30 Polybutylene Terephthalate 30% Glass fiber Reinforced PBT GF is a highly versatile, semi-crystalline structural thermoplastic reinforced with 30% glass fiber, with very high rigidity and strength characteristics and excellent electrical insulation prop.. |
|||
| CTE, linear | 20.0 µm/m-°C @Thickness 0.0508 mm |
11.1 µin/in-°F @Thickness 0.00200 in |
First heat; ASTM-D696 |
| 3M 9672 Adhesive Transfer Tapes with Adhesive 300 3M™ Adhesive Transfer Tapes with 3M™ Adhesive 300 offer excellent adhesion to a wide variety of surfaces, including low surface energy plastics and foam. This pressure sensitive acrylic adhesive f.. |
|||
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM E831 |
| BASF Ultramid® B3EG3 15% Glass Filled PA6 (Dry) Description: 15% glass-fiber reinforced injection-molding grade with enhanced impact resistance, for example, for vehicle mirror housings as well as for the wheels of mountain bikes.Information prov.. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CENTROPLAST CENTROMID 12 GF 30 Polyamide 12 30% glass fiber CENTROMID 12 GF 30 is a dimensionally stable and high strength material with good electrical insulating properties. Its applications include levers and valve parts.Information provided by CENTROPLA.. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Teijin Panlite® BN-8120R Improved Mold Release, Carbon Fiber Reinforced, Flame Resistant Polycarbonate Resin CF 20% reinforced grade, meeting UL 94 V-2. It has excellent strength, stiffness, heat resistance and electric conductivity. Other features are flame retardance, low molding shrinkage and dimensiona.. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Teijin Panlite® G-3430R Glass Fiber Reinforced Polycarbonate Resin GF 30% reinforced and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecision machinery components th.. |
|||
| CTE, linear | 20.0 - 40.0 µm/m-°C | 11.1 - 22.2 µin/in-°F | Average value: 27.7 µm/m-°C Grade Count:14 |
| Overview of materials for Nylon 46, Flame Retarded + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Flame Retarded + Glass Fiber Reinforced". Each property range of values reported is minimum an.. |
|||
| CTE, linear | 20.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |
| A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane Information provided by A. Schulman. |
|||