Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika B2040G50 PA66, 50% Glass Fiber Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.20 mm |
0.0020 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039 |
| Tensile Strength at Break | 220 MPa | 31900 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 16.7 GPa | 2420 ksi | ISO 527-1/-2 |
| Flexural Strength | 360 MPa | 52200 psi | ISO 178 |
| Flexural Modulus | 13.5 GPa | 1960 ksi | ISO 178 |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 486 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 233 °C | 451 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG37CR ABS
- Niche Polymer PA66GF43N Nylon 66, 43% Glass Fiber Filled
- PolyOne Bergamid™ B700 UF Polyamide 6 (Nylon 6)
- SABIC Innovative Plastics Lexan® FXD1414T PC Copolymer (Europe-Africa-Middle East)
- Loxim 800 00 HB Polypropylene Compound, Flame Retardant
- Lanxess Durethan® AKV 35 HR H2.0 901510 Nylon 66, Glass Fiber Reinforced
- Lanxess Pocan® B 3225 000000 PBT, 20% Glass Fiber
- Teknor Apex APEX® 65015 Polyvinyl Chloride, Flexible
- 3M 3311 General Purpose Aluminum Foil Tape
Copyright © lookpolymers.com All Rights Reserved