Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.18 mm |
545 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Annealed; ASTM D648 |
PolyOne Edgetek® PK-20GF/000 Polyetheretherketone (PEEK), Glass Filled
(discontinued **) Description/Features:Glass Fiber ReinforcedUL 94 (CTI Testing)PolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | |
Lehmann & Voss LUVOCOM® 1105-8278/GY PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Ch.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | |
Lehmann & Voss LUVOCOM® 1105/GF/20/EM/BK PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Ch.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | |
Lehmann & Voss LUVOCOM® 1105-0948/YL2 PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Ch.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ISO 75-2/A |
Solvay Specialty Polymers Amodel® A-1130 FW Polyphthalamide (PPA), 30% Glass Fiber Amodel® A-1130 FW is a 30% glass-fiber reinforced polyphthalamide (PPA) grade containing a solid lubricant. This resin was designed for moderate-pressure, low-velocity friction and wear applicati.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA4/6 CF30 30% Carbon Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 30% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedInformation provided by TP Composites.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA4/6 CF40 HS 40% Carbon Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 40% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedInformation provided by TP Composites.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ASTM D648 |
Techmer ES HiFill® PA4/6 GF50 ML2 50% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 50% Filler by WeightAdditive: Molybdenum Disulfide LubricantFeatures: LubricatedAppearance: BlackUL File Num.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ASTM D648 |
Techmer ES Luriblend® PA4/6 CF30 TL15 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance and Low FrictionInformation p.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP UC006H PPA LNP THERMOCOMP* UC006H is a compound based on Polyphthalamide resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP UF00ASW PPA LNP* Thermocomp* UF00ASW is a compound based on Polyphthalamide (PPA) containing glass fiber. Characteristics of this grade of Heat Stabilized and Hot Water Moldable. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | dry; ISO 75-1/-2 |
DSM Stanyl® TW242FM10 PA46-(GF+MF)50 50% Glass/Mineral Reinforced, Heat Stabilized |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | dry; ISO 75-1/-2 |
DSM Stanyl® TW271F8 (PA46+PTFE)-GF40 40% Glass Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ISO 75-1/-2 |
DSM Stanyl® TW275F6 (DAM) Nylon 46 30% Glass Reinforced, Heat Stabilized, Molydisulfide Lubricated (North America) Information provided by DSM Engineering Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® HT2VZ-33H PA6T/66-GF33 Product description: Grivory HT2VZ-33H is a 33% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT2VZ-33H is an injecti.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® HT1V-5 HY black 9205 PA6T/6I-GF50 Product description: Grivory HT1V-5 HY black 9205 is a 50% glass-fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT1V-5 HY bl.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® HTV-5H1 nat PA6T/6I-GF50 Product description: Grivory HTV-5H1 natural is a 50% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I. Ac.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ASTM D648 |
Kuraray Genestar™ GR2300 Nylon, 30% Glass Filled Standard V-0 Grade. Delivers increased fluidity and weld strength. Well suited for a wide range of electrical and electronic components. |