Techmer ES LuriblendÂ® PA4/6 CF30 TL15 30% Carbon Filled

Category	Polymer , Thermoplastic , Nylon , Nylon 46
Manufacturer	Techmer ES
Trade Name	Luriblend®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES LuriblendÂ® PA4/6 CF30 TL15 30% Carbon Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance and Low FrictionInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/inÂ³	ASTM D792
Water Absorption	2.0 % @Time 86400 sec	2.0 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	186 MPa	27000 psi	ASTM D638
Elongation at Break	2.6 %	2.6 %	ASTM D638
Flexural Strength	283 MPa	41000 psi	ASTM D790
Flexural Modulus	16.5 GPa	2400 ksi	ASTM D790
Izod Impact, Notched	0.694 J/cm @Thickness 3.17 mm	1.30 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	27.0 Âµm/m-Â°C	15.0 Âµin/in-Â°F	ASTM D696
Melting Point	295 Â°C	563 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	293 Â°C	560 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	285 Â°C	545 Â°F	Unannealed; ASTM D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	10 ohm-cm	10 ohm-cm	ASTM D257