SABIC Innovative Plastics LNP THERMOCOMP UC006H PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UC006H PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* UC006H is a compound based on Polyphthalamide resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| 1.324 g/cc | 0.04783 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.310 % | 0.310 % | 50% RH, 24 hrs; ASTM D570 |
| 0.660 % | 0.660 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm @Time 86400 sec |
0.0016 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0062 cm/cm @Time 86400 sec |
0.0062 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 263 MPa | 38100 psi | ISO 527 |
| 287 MPa | 41600 psi | ASTM D638 | |
| Elongation at Break | 1.3 % | 1.3 % | ISO 527 |
| 1.5 % | 1.5 % | ASTM D638 | |
| Tensile Modulus | 26.11 GPa | 3787 ksi | 50 mm/min; ASTM D638 |
| 28.16 GPa | 4084 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 413 MPa | 59900 psi | ISO 178 |
| 419 MPa | 60800 psi | ASTM D790 | |
| Flexural Modulus | 22.32 GPa | 3237 ksi | ISO 178 |
| 22.63 GPa | 3282 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.27 J/cm | 15.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.27 | 0.27 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.21 | 0.21 | ASTM D3702 Modified |
| K (wear) Factor | 12.1 x 10-8 mm³/N-M | 6.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 18.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.5 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 39.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 40.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GF 924 33 UV Black 108 Polyamide 66 (Nylon 66)
- Formosa Plastics Formolene® FORMAX® L71709A Film (Hexene Grade) LLDPE (discontinued **)
- Sharadaa Ceramics Sharada RFC-45 Gel Bonded Castables
- Star Plastics PC1212FRR Molding Grade PC FR
- Skamol Group SUPER 1100 E Calcium Silicate Insulating Slab
- SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA (Asia Pacific)
- Formosa Plastics Formolene® 4100P Injection Molding Polypropylene
- ExxonMobil Escorene® LL-3201 LLDPE/Hexene Premium High Strength 1.2 mil Film, Stiff (discontinued **)
- Gromax CFG33-QS11N1 Nylon 6 33% Glass Filled (Conditioned)
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C
Copyright © lookpolymers.com All Rights Reserved