- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 536 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 536 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| Quadrant EPP Duratron® PAI T4501 PAI + graphite + PTFE, compression moulded (ISO Data) Compression moulded Duratron T4501 PAI is similar in composition to Duratron T4301 PAI, and is selected when larger shapes are required Very high maximum allowable service temperature in air (250°C.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | |
| Lehmann & Voss LUVOCOM® 19-7221/OR Polyamide 46, with glass fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Highly dimensionally stable at elevated temperatures.Gear parts for automot.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | |
| LATI Laramid G/45 PPA, 45% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | |
| LATI Laramid G/50 PPA, 50% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA (Europe-Africa-Middle East) LNP* LUBRICOMP* UFL36AS is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features include Internally Lubricated, Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber Amodel® AE-1133 is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) designed to work in the modern automotive electrical environment. It has a high heat deflection temperature, high .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers Amodel® AT-1125 HS Polyphthalamide (PPA), 25% Glass Fiber (Dry) Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 280 °C | >= 536 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP LF006EL PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LF006EL is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features include: Easy Molding. FDA Compliant Raw Materials. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 280 °C | >= 536 °F | Post Baked; ASTM D648A |
| Sumitomo Bakelite North America E 3812M-1 Mineral and Glass Filled Electrical Encapsulation Grade Epoxy E 3812M-1 is a mineral and short fiberglass filled epoxy molding compound for low pressure encapsulation molding, featuring excellent dimensional stability, good thermal shock resistance, and good e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 280 °C | >= 536 °F | Post Baked; ASTM D648A |
| Sumitomo Bakelite North America EM 7302XLD Long Glass Fiber Reinforced Epoxy EM 7302XLD is a long fiberglass reinforced epoxy molding compound with a low density inert filler. This compound is designed for applications where moderate strength and weight savings are desirable.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | As Molded; ASTM D648A |
| Sumitomo Bakelite North America Epiall® 1904B-1 Short Glass Fiber Reinforced Epoxy Epiall 1904B-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties.Information provided .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | As Molded; ASTM D648A |
| Sumitomo Bakelite North America RX® 640 Fiberglass Reinforced Phenolic Resole RX 640 is a fiberglass reinforced, ammonia-free, phenolic resole compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type GPI-5.Information supp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | As Molded; ASTM D648A |
| Sumitomo Bakelite North America RX® 643 Fiberglass Reinforced Phenolic RX 643 is a fiberglass reinforced, ammonia-free, phenolic resole compound, with good dimensional stability and good strength at elevated temperatures. Meets ASTM D-5948 Type GPI-10.Information pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 280 °C | >= 536 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK (Europe-Africa-Middle East) LNP* THERMOCOMP* LF006 is a compound based on Polyetheretherketone resin containing Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT2V-3H LF PA*-GF30 Grivory TH2V-3H LF is a glass fiber reinforced (30%), PTFE modified engineering thermoplastic based on semi-crystalline partially aromatic copolyamide. Polymer designation acc. ISO: PA6T/66 Polymer .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT2V-5H PA6T/66-GF50 Product description: Grivory HT2V-5H is a 50 % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Polymer designation acc. to ISO:.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HTV-3H1 black 9205 PA6T/6I-GF30 Product description: Grivory HTV-3H1 black 9205 is a 30% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HTV-4H1 black 9205 PA6T/6I-GF40 Product description: Grivory HTV-4H1 black 9205 is a 40% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT1V-3 FWA black 9225 PA6T/6I-GF30 Product description: Grivory HT1V-3 FWA black 9225 is a 30 wt.- % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT1V-4 FWA black 9225 PA6T/6I-GF40 Product description: Grivory HT1V-4 FWA black 9225 is a 40 wt.- % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ASTM D648 |
| Clariant Renol PPSS0007 Polyphenylene Sulfide, Glass Fiber and Mineral Filled Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | dry; ISO 75-1/-2 |
| DSM Stanyl® TW241F5 PA46-GF25 Heat Stabilized, 25% Glass Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ASTM D648 |
| LATI LARPEEK 50 G/20 20% Glass Reinforced Polyetheretherketone (PEEK)
(discontinued **) Larpeek polyetheretherketone (PEEK) is a high performance thermoplastic offering cost effective performance in difficult environments across all industries. PEEK is temperature resistant (up to 250°.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT1V-3 HY black 9205 PA6T/6I-GF30 Product description: Grivory HT1V-3 HY black 9205 is a 30% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT1V-3 HY bl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT1V-4 FWA nat PA6T/6I-GF40 Product description: Grivory HT1V-4 FWA natural is a 40 wt.-% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 |
| Quadrant EPP Duratron® PAI T5530 PAI, 30% glass fibers, compression moulded (ISO Data) This 30 % glass fibre reinforced grade offers higher stiffness, strength and creep resistance than the Duratron PAI grades mentioned above. It is well suited for structural applications supporting s.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | As Molded; ASTM D648A |
| Sumitomo Bakelite North America Epiall® 1914A Short Glass Fiber Reinforced Epoxy Epiall 1914A is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties.Information provided by.. |
|||