LATI Laramid G/50 PPA, 50% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Laramid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laramid G/50 PPA, 50% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.64 g/cc
0.0592 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0045 - 0.0070 cm/cm
0.0045 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa

@Temperature 150 °C
 13800 psi

@Temperature 302 °F
155 MPa

@Temperature 120 °C
 22500 psi

@Temperature 248 °F
185 MPa

@Temperature 90.0 °C
 26800 psi

@Temperature 194 °F
205 MPa

@Temperature 60.0 °C
 29700 psi

@Temperature 140 °F
260 MPa

@Temperature 23.0 °C
 37700 psi

@Temperature 73.4 °F
Elongation at Break 2.1 %

@Temperature 23.0 °C
 2.1 %

@Temperature 73.4 °F
2.3 %

@Temperature 60.0 °C
 2.3 %

@Temperature 140 °F
2.4 %

@Temperature 90.0 °C
 2.4 %

@Temperature 194 °F
3.8 %

@Temperature 120 °C
 3.8 %

@Temperature 248 °F
6.5 %

@Temperature 150 °C
 6.5 %

@Temperature 302 °F
Tensile Modulus 1.10 GPa

@Temperature 120 °C
 160 ksi

@Temperature 248 °F
6.00 GPa

@Temperature 150 °C
 870 ksi

@Temperature 302 °F
12.5 GPa

@Temperature 90.0 °C
 1810 ksi

@Temperature 194 °F
14.5 GPa

@Temperature 60.0 °C
 2100 ksi

@Temperature 140 °F
17.5 GPa

@Temperature 23.0 °C
 2540 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 7.50 J/cm²
35.7 ft-lb/in²
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 150 °C
302 °F
Deflection Temperature at 0.46 MPa (66 psi) 290 °C
554 °F
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Vicat Softening Point 275 °C

@Load 5.00 kg
 527 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 310 - 340 °C
590 - 644 °F
Mold Temperature 150 - 170 °C
302 - 338 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa