- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 486 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 486 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Unannealed; ISO 75-2/A |
| PolyOne OnForce™ LFT NN-30LCF/002 Grey Polyamide 66 (Nylon 66) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Unannealed; ISO 75-2/A |
| PolyOne OnForce™ LFT NN-50LGF/000 HS UV Black Polyamide 66 (Nylon 66) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.18 mm |
486 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne Edgetek® NN-30GF/000 Polyamide 66 (Nylon 66) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.18 mm |
486 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ GF 1200 A 43 Natural Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 70G25HSLR NC010 Nylon 66
(Unverified Data**) Zytel® 70G25HSLR NC010 is a 25% glass fiber reinforced, heat stabilized, hydrolysis resistant polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP RFN1ASXS PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFN1ASXS is a compound based on Nylon 66 resin containing Glass Fiber, MOS2. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-848 Polyaryletherketone (PAEK) AvaSpire® AV-848 is a high-temperature, polyaryletherketone (PAEK) that offers several key performance advantages over comparable grades of PEEK above 150°C, including better dimensional stabi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Stat-kon REL36 PA 66 LNP* Stat-Kon* REL36 is a compound based on Nylon 6/6 containing carbon fiber and PTFE. Characteristics of this grade are Statically Conductive.This data was supplied by SABIC-IP for the Americas r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RC008H PA 66 LNP THERMOCOMP* RC008H is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF006XXY PA 66 LNP* Thermocomp* RF006XXY is a compound based on Nylon 66 containing 30% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RF008XXZ PA 66 LNP THERMOCOMP* RF008XXZ is a compound based on Nylon 66 resin containing 40% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RX10405H PA 66 LNP* Thermocomp* RX10405H is a compound based on Nylon 6/6 containing Carbon Fiber. Characteristics of this grade are: Healthcare. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON OE006C1 PPS - Linear LNP* STAT-KON* OE006C1 is a compound based on PPS - Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON RX06479 PA 66 (Asia Pacific) LNP VERTON* RX06479 is a compound based on Nylon 66 resin containing Long Glass. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| A. Schulman Aqualoy® 645 Glass Fiber Reinforced Hydrolysis Resistant Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| DuPont Performance Polymers VESPEL TP-8169 Polyimide DuPont Vespel TP-8169 parts are specified for high-temperature applications. TP-8169 parts offer a unique balance of mechanical and thermal properties for high performance in aggressive environments.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 70G35NOX BK309 Nylon 66 Zytel® 70G35NOX BK309 is a 35% glass reinforced, polyamide 66 resin developed for Selective Catalytic Reduction applications that require exposure to water/urea solution.Information provided by DuP.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| E-Polymers TEKAMID® TA210GR , 33% Glass Fiber Reinforced PA66, DAM 33% Glass Fiber reinforced, Anti EG, Anti HydrolysisInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ISO 75-2/A |
| Ascend Performance Materials VYDYNE® R543 Nylon, 43% Glass Reinforced, DAM Vydyne® R543 is general purpose, 43% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine fee, flow and mold release. Glass.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ISO 75-2/A |
| Ascend Performance Materials Vydyne® R543H Nylon 66, 43% Glass Filled, Dry as Molded Vydyne® R543H is general-purpose, 43% glass-reinforced PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for improved machine feed, flow and mold release. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| Ashley Polymers Ashlene® 528L-5G Nylon 66, 5% Glass Reinforced General purpose glass fiber reinforced nylon, designed for parts requiring improved dimensional stability and higher strength than conventional resins.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| Asia International Enterprise (Hong Kong) 60G8-43GF Nylon 66, 43% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| A. Schulman ComAlloy E-16901B PPS Alloy, Electrically Conductive - Carbon Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| A. Schulman ComAlloy E-16902N PPS Alloy, Electrically Conductive - Stainless Steel Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP VERTON RX06479 PA 66 LNP VERTON* RX06479 is a compound based on Nylon 66 resin containing 35% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, UV Stabilized, Structural |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 70G35HSRX BK099 Nylon 66
(Unverified Data**) Zytel® 70G35HSRX BK099 a 35% glass reinforced, heat stabilized, hydrolysis resistant PA66 for injection molding. Developed for applications designed for direct overmolding of gaskets onto thermopla.. |
|||