SABIC Innovative Plastics LNP STAT-KON OE006C1 PPS - Linear
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON OE006C1 PPS - Linear.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* OE006C1 is a compound based on PPS - Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.00080 - 0.0010 cm/cm @Time 86400 sec |
0.00080 - 0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 173 MPa | 25100 psi | 5 mm/min; ISO 527 |
| 192 MPa | 27800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 21.97 GPa | 3186 ksi | 1 mm/min; ISO 527 |
| 23.54 GPa | 3414 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 263 MPa | 38100 psi | ISO 178 |
| 269 MPa | 39000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 19.64 GPa | 2849 ksi | 2 mm/min; ISO 178 |
| 19.9 GPa | 2890 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.42 J/cm | 8.28 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
4.44 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 275 °C | 527 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 277 °C @Thickness 3.20 mm |
531 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 264 °C @Thickness 3.20 mm |
507 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Murtfeldt Original Material ”S”® plus + Bright ESD Polyethylene, Conductive
- Nylene® 452 Nylon 6
- ICO Polymers ICORENEâ„¢ 190-1332 LMDPE Rotational Molding Resin
- Indium Corp. Sn992 Pb-Free Soldering Alloy
- LTL Color Compounds ColorRxâ„¢ PP1-2000RX Biocompatible Polypropylene Homopolymer
- Solvay Specialty Polymers Omnix® 9050 Polyamide, High Performance (HPPA), 50% Glass Fiber
- Polyram PA310G8 Nylon 66, 40% Glass Fiber Reinforced, Heat Stabilized
- TIMET TIMETAL® 230 Titanium Alloy (Ti-2.5Cu); Annealed
- DuPont Teijin Films Teonex® Q51 Polyester Film, 48 Gauge
- CPT C-Flex® R70-089 Opaque Biocompatible TPE
Copyright © lookpolymers.com All Rights Reserved