- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 424 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 424 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | STN EN ISO 75-2 (A) |
| Plastcom SLOVAMID® 6 GF 65/2M PA6 reinforced with glass fiber PA 6 for injection molding, reinforced with 65% of glass fiber, for moldings used in the automotive, electrical, engineering and consumer-goods industry. Application: grips of electrotools, hobby to.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Ovation Polymers UTTAP QU HT530 GF Nylon, 30% Glass Reinforced Glass reinforced (30 %) - High Temperature Polyamide Alloy, excellent chemical and electrical resistance, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Enduran 7062X PBT+PET (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ASTM D648 |
| Shell Carilon® DP R1130 Polyketone, 30% Glass Fiber Reinforced
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP R1130 is a 30 percent glass fiber reinforced compound based on a developmental e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | |
| Reliance Industries PBT - 35% Glass filled Information provided by Reliance Industries |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | |
| Cookson Group Plaskon® 3100 Novolac Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A flame retardant, novolac-hardened epoxy molding compound recommended for semiconductor packages that are not stress sensitive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 73G45 BK263 Nylon 6
(Unverified Data**) Zytel® 73G45 BK263 is a 45% glass fiber reinforced, black polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM CRS5201 PEI 20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM CRS5201 PEI (Asia Pacific) 20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming, UL94 V0 and 5VA listing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM CRS5201R PEI 20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM CRS5201R PEI (Asia Pacific) 20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem CRS5211 PEI 20% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming, UL94 V0 and 5VA listing.Th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM CRS5311 PEI 30% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM CRS5711 PEI (Asia Pacific) 15% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5VA listing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON RX04031 PA 66 (Europe-Africa-Middle East) LNP* STARFLAM* RX04031 is a compound based on PA66 resin containing Carbon Fiber, Glass Fiber, Flame Retardant. Added features include: Non-Brominated & Non-Chlorinated Flame Retardant, Electricall.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | |
| Shinil Chemical SHINCON PES-CNT LCD Rack LCD Rack is used to transfer or bake LCD frame in the electronic assembly or LCD packaging assembly line. Current LCD Rack is made of poly ether ether ketone (PEEK) with carbon fiber (CF). Since b.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP JF004 PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004 is a compound based on Polyethersulfone resin containing Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Europe-Africa-Middle East) LNP* Thermocomp* JF004E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP JF004LZ PES LNP* Thermocomp* JF004LZ is a compound based on PES containing 20% Glass Fiber. Added features include: Extrusion Grade, Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP JX97000 PES (Europe-Africa-Middle East) LNP* Thermocomp* JX97000 is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | Absolute Drying; ASTM-D648 |
| Toyobo GLAMIDE® TY-181GC Nylon/Elastomer GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Rynite® FR531 NC010 Polyethylene Terephthalate (PET)
(Unverified Data**) 36% Reinforced Flame Retardant Polyethylene Terephthalate Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® 73G45 BK263 Nylon 6
(Unverified Data**) 45% Glass Reinforced Polyamide 6 Zytel 73G45 BK263 is a 45% glass fiber reinforced black polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Rynite® 408 BK515 PET Rynite® 408 BK515 is a 30% glass reinforced modified polyethylene terephthalate with improved impact resistance. Excellent balance of strength, stiffness, toughness and temperature resistance.Info.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ASTM D648 |
| Azdel AZMET® CM20350 35% continuous random fiber mat / PBT resin matrix AZDEL® CM20350 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a Polybutylene Terephthalate (PBT) resin matrix. This composite material fea.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ASTM D648 |
| Ashley Polymers Ashlene® 559LD-33G Nylon 66, 33% Glass Reinforced A high impact reinforced nylon copolymer with good low temperature properties.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ASTM D648 |
| Ashley Polymers Ashlene® 990L-50G Nylon 610, 50% Glass Reinforced 50% glass reinforced, excellent dimensional stability and low water absorption. Also available as: 990LS-50G, same with heat stabilizer.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ASTM D648 |
| PolyOne Edgetek® NI-30CF/000 Nylon 6/10 - 30% Carbon Fiber Reinforced
(discontinued **) Data provided by PolyOne. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ASTM D648 |
| PolyOne Edgetek® NI-40CF/000 Nylon 6/10 - 40% Carbon Fiber Reinforced
(discontinued **) Data provided by PolyOne. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 424 °F | ASTM D648 |
| Plenco 50335 PET, Pellet, Injection Molded, White
(discontinued **) PLENCO 50335 is an engineering grade glass reinforced polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed and available in white, natural, and black.Inform.. |
|||