SABIC Innovative Plastics Ultem CRS5211 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem CRS5211 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D 792 |
| Melt Flow | 5.1 g/10 min @Load 6.60 kg, Temperature 337 °C |
5.1 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 137 MPa | 19900 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 6.89 GPa | 999 ksi | 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 213 MPa | 30900 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.850 J/cm @Temperature 23.0 °C |
1.59 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 4.80 J/cm @Thickness 3.20 mm |
8.99 ft-lb/in @Thickness 0.126 in |
reverse notched; ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 |
| 5VA @Thickness 1.47 mm |
5VA @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten, PLC code 5; ASTM D 495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | PLC code 4; UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | PLC code 0; UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | surface, PLC code 4; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | PLC code 3; UL 746A |
Users viewing this material also viewed the following:
- Polymer Industries Densetec HDPE Marine Board
- Polimeri Europa Flexirene® MS 40 A Linear Low Density Polyethylene
- SABIC Innovative Plastics Lexan® XHT2146 PC Copolymer (Asia Pacific)
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Sheet (0.250" thick)
- Total PPH 3862 Homopolymer Polypropylene, Fiber Grade
- Diamond Polymers ABS 4011 HH
- BASF Heligoen® Green L 8731 Color Additive
- Colorite Polymers 5514 General Purpose Vinyl Compound
- Dow Corning 3-0134 Polymer 50,000 CS
- Resirene Resirene® 6110 High Impact Polystyrene
Copyright © lookpolymers.com All Rights Reserved