- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 345 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 345 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Nylene® PA6/6 Mineral Filled 6440 HS Nylon 6/6 34% Mineral Filler; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Oxford Polymers Polysulfone PSF P170-64170 White PSU Product Description: Polysulfone injection molding grade, precolored white Processing and Delivery Form: Pellets and Injection Molding Special Characteristics: Continuous use up to 300(f)Informatio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Niche Polymer PPHT40BK Homopolymer PP, 40% Talc Fiber Filled Information provided by Niche Polymer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Polymer Resources TP-FRG15 Polybutylene Terephthalate, 15% Glass Reinforced, Flame Retardant Polybutylene Terephthalate, 15% Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Asia Pacific) LNP KONDUIT* PTF2BXXX is a compound based on Nylon 6 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C @Thickness 3.20 mm |
345 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP COLORCOMP G1000 PSU LNP* COLORCOMP* G1000 is an unfilled Polysulfone resin. Added feature of this grade is: Transparent. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C @Thickness 3.20 mm |
345 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP KONDUIT PX11422 PA 6 LNP* KONDUIT* is a compound based on Nylon 6 resin containing thermally conductive fillers. Added feature of this material is Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 - 183 °C | 345 - 362 °F | Average value: 178 °C Grade Count:13 |
| Overview of materials for Polysulfone, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polysulfone, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are incl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Udel® P-1700 Polysulfone (PSU)
(Unverified Data**) Udel P-1700 polysulfone (PSU) is a tough, rigid, high-strength thermoplastics suitable for continuous use up to 300°F (149°C). It is resistant to oxidation and hydrolysis and withstand prolonged e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Udel® P-1700 LCD Polysulfone (PSU)
(Unverified Data**) Udel P-1700 LCD polysulfone is especially well suited for the fabrication of porous membranes for filtration applications. The membranes are usually in the form of hollow fibers, but tube, plate or .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Udel® P-1710 Polysulfone (PSU)
(Unverified Data**) Udel P-1710 polysulfone (PSU) is a tough, rigid, high-strength thermoplastic that is suitable for continuous use up to 300°F (149°C). The resin is resistant to oxidation and hydrolysis and withsta.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Plenco 4100 Phenolic, Granular, Injection Molded
(discontinued **) Two-stage Phenolic. PLENCO 04100 is a black two stage, medium heat resistant phenolic molding compound. It has excellent moldability characteristics and molded finish. It is used in appliance and .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ISO 75 |
| GEHR Plastics PSU Polysulfone Polysulfone shows great thermal stability. It possesses a high mechanical strength, very good dielectric properties and hydrolysis resistance and a high radiation resistance. PSU has a low notch imp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C @Thickness 3.20 mm |
345 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP SFL2A PA12 LNP* LUBRICOMP* SFL2A is a compound based on Nylon 12 resin containing 50% Glass Fiber, 10% PTFE. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Ajedium™ Films -- Udel® PSU P-1700 NT-11 Polysulfone (PSU) Udel® P-1700 polysulfones are tough, high-strength thermoplastics that are suitable for continuous use up to 300°F (149°C). Udel Film is resistant to oxidation and hydrolysis and withstand .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Udel® P-1700 LCD Polysulfone (PSU) Udel® P-1700 LCD polysulfone is especially well suited for the fabrication of porous membranes for filtration applications. The membranes are usually in the form of hollow fibers, but tube, plate.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Udel® P-3703 Polysulfone (PSU) Udel® P-3703 is a high-flow grade of polysulfone intended for injection molding applications with thin walls or long flow lengths. This grade has higher flow than Udel® P-1700 and a slightly g.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing 20% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp HX05073 PA 11 LNP THERMOCOMP* HX05073 is a compound based on Nylon 11 resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Plenco 1500 Polyester, Granular, Transfer Molded PLENCO 01500 is a general purpose, mineral filled granular polyester molding compound, offering excellent arc and track resistance, and low post shrinkage characteristics. UL recognized under compon.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Unannealed; ASTM D648 |
| PolyOne Edgetek® PF-1000 Polysulfone
(discontinued **) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| Plaslok 504 Black (COM) Heat Resistant Mineral/Cellulose Filled Phenolic Molding Compound
(discontinued **)&l Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 504 is a two-stage, mineral and cellu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU (Asia Pacific) LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing Glass Fiber. |
|||