Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 243 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	469 °F	ASTM D648
PlastiComp Complet® LCF30-PA66 30% Long Carbon Fiber This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc.
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	469 °F	ASTM D-648
PlastiComp Velocity® LGF60-PA66 High Flow Nylon 66, 60% Long Glass Fiber This compound complies with European Union Directive 2002/95/EC Restriction of Hazardous Substances (RoHS).Information provided by PlastiComp, Inc.
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	470 °F	ASTM D648
Polymer Resources NY66-IMG33 Nylon, 33% Glass Reinforced, Impact Modified (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide..
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	469 °F	ASTM D648
PTS Trimid® N66-G13L 13% Glass Fiber Reinforced Lubed Nylon 6/6 Information provided by Polymer Technology and Services, LLC (PTS).
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	470 °F	Unannealed, 0.125 in bars; ASTM D648
PolyOne Edgetek® LC-30GF/000 LCP (Liquid Crystal Polymer), 30% Glass Reinforced, Hi-Temp (discontinued **)< Information provided by PolyOne™ Corporation
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	469 °F	ASTM D648
PolyOne Edgetek® LCP-30GF/000 Liquid Crystal Polymer - 30% Glass Fiber (discontinued **) Data provided by PolyOne.
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	470 °F	Unannealed; ASTM D648
Ravago Manufacturing Americas Hylon® N1020HL BK Nylon 6/6 (discontinued **) Available in North America Filler: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedForm: Pellets Processing Method: I..
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	470 °F	Unannealed; ASTM D648
Ravago Manufacturing Americas Hylon® N1033TL Nylon 6/6 (DAM) (discontinued **) Information provided by Ravago.
Deflection Temperature at 1.8 MPa (264 psi)	243 Â°C	469 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE.
Deflection Temperature at 1.8 MPa (264 psi)	243 Â°C	469 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-KON OCL13XXP PPS - LINEAR (Europe-Africa-Middle East) LNP* Stat-kon* OCL13XXP is a compound based on PPS - LINEAR resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi)	243 Â°C	469 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RF006H PA 66 LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare.
Deflection Temperature at 1.8 MPa (264 psi)	243 Â°C	469 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RF006XXZ PA 66 LNP THERMOCOMP* RF006XXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber
Deflection Temperature at 1.8 MPa (264 psi)	243 Â°C	469 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 LNP* THERMOCOMP* RF00AH is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added feature of this grade is: Healthcare.
Deflection Temperature at 1.8 MPa (264 psi)	243 Â°C @Thickness 3.20 mm	469 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 LNP* THERMOCOMP* RF00AH is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added feature of this grade is: Healthcare.
Deflection Temperature at 1.8 MPa (264 psi)	243 Â°C @Thickness 3.20 mm	469 Â°F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66 (Asia Pacific) LNP* Thermocomp* RF00AH is a compound based on Nylon 66 resin containing Glass Fiber.
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	470 °F	ASTM D648
Clariant Renol PA113G33HR Nylon 66, 33% Glass Fiber, Heat Stabilized, Hydrolysis Resistant Data provided by Clariant Masterbatches
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	469 °F	ASTM D648
Ashley Polymers Ashlene® 541-33G Nylon 66, 33% Glass Reinforced Nylon 66, 33% glass reinforced for extrusion applications.Data provided by the manufacturer
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	469 °F	ASTM D648
Chem Polymer Chemlon 115 G Nylon 66, 15% Glass Fiber Reinforced A 15% glass fiber reinforced nylon 66 offering improved creep resistance, stiffness, tensile strength and dimensional stability over unmodified nylon 66 materials. This product offers slight improv..
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	469 °F	ASTM D648
A. Schulman ComAlloy Lubrilon® 636 Nylon 6/6, Carbon Fiber Reinforced, Proprietary Lubricant Package Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	469 °F	DAM; ASTM D648
DuPont Performance Polymers Zytel® FR70G25V0 NC010 Nylon 66 (Unverified Data**) Zytel® FR70G25V0 NC010 is a 25% glass fiber reinforced, heat stabilized, flame retardant polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Deflection Temperature at 1.8 MPa (264 psi)	243 °C	469 °F	ASTM D-648
PlastiComp Complet® LGF20 - PA66 Nylon 66, 20% Long Glass Fiber Reinforced Complet® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Nylon 66 with 20% long glass fiber reinforcementInformation provided by PlastiComp, Inc.