- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 215 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 215 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Nilit FRIANYL B63 CU90 Nylon 6.6 for injection molding, 90% copper filled Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Asia Pacific) Thermally conductive mineral filled PA6 FR compounding |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | |
| Plastcom SLOVAMID 6 NG GF 20 HLS PA6, 20% glass fibre, combined stability FeaturesPA 6 for injection moulding, chemically reinforced with 20% glass fibre, heat stabilized and weather stabilized. Stabilized against hydrolysis. Good surface finisch.Packaging, transport, sto.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Nilit FRIANYL B63 GV35 Nylon 6 for injection molding, 35% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1,-2 |
| Gromax BBG30-AN00N1 Nylon 6, Flame Retardant (Dry) Information provided by Gromax Enterprises Corp. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | |
| LATI Later 4 K/30 PBT, 30% Carbon Fiber Reinforced Polybutylene Terephthalate (PBT) based compound. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplasti.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Ultem 1000RV PEI (Europe-Africa-Middle East) Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Europe-Afr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM CRS5111 PEI (Asia Pacific) 10% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5 VA listing. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics ULTEM HU1000 PEI Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI).. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PBT GF30 BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAppearance: BlackTPCI# 9864111Information provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp JF003L PES LNP* Thermocomp* JF003L is a compound based on Polyethersulfone (PES) containing Glass Fiber. Characteristics of this grade are Low Extractable.This data was supplied by SABIC-IP for the Americas r.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-93 |
| Wellman EcoLon® MRGF1914-BK1 Nylon 66, 40% Mineral and Glass Reinforced All information provided by Wellman Engineered Resins. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Toyobo VYLOPET® EMC132-02 Injection Molding Polyester Resin, Flame Resistant Applications: Relay partsFeatures: Excellent arc resistanceFlame resistanceInformation provided by Toyobo. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Toyobo VYLOPET® EMC310TU Injection Molding Polyester Resin, Warpageless, High cycles Applications: Coiled bobbinsMouthpiecesFeatures: High cyclesWarpagelessInformation provided by Toyobo. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| DSM Akulon® K224-G0 Nylon 6-50% Glass Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® G4V-5H black 9915 PA*-GF50 Product description: Grivory G4V-5H is a 50% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline partially aromatic copolyamide. Grivory G4V-5H is used for injectio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® G4V-5H nat PA*-GF50 Product description: Grivory G4V-5H is a 50% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline partially aromatic copolyamide. Grivory G4V-5H is used for injectio.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® TSGZ-30 PA666-GF30 Product description: Grilon TSGZ-30 is a heat stabilized, normal viscosity, and impact modified PA66 + PA6 injection molding grade with 30% glass fibers. Grilon TSGZ-30 has the following important p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® HTN FR55G50NHLW BK046 Polyphthalamide (PPA)
(Unverified Data**) 55% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide with Low Warpage and High Stiffness Zytel HTNFR55G50NHLW BK046 is a 50% glass reinforced flame retardant high perf.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Eurotec® Tecomid® NB40 GR45 NL HS PA6, 45% glass fiber reinforced, heat stabilized, natural Information provided by Eurotec® |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| E-Polymers Tekaster® F615GM , 40% GF/MF Reinforced PET 40% GF/MF Reinforced, Low warpageInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | HDT/A; ISO 75-2 |
| Akro-Plastic Akromid® B3 GF 35 (2473) PA 6 Dry, 35% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| E-Polymers SEPAZ® LB40 PA6 LFT Resin Long Fiber Thermoplastics: SEPAZ LFT products, injection moldable long fiber-reinforced thermoplastics (LFT), are made using a unique pultrusion that thoroughly wets out the glass fibers and deliver.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | |
| LATI Latiohm 66-04 PD01 G/25-V0CT1 PA66, 25% Glass Fiber Reinforced, Flame Retardant Semiconductive/dissipative product based on Polyamide 66 (PA66). Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific;.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | As Molded; ISO 75 A |
| Sumitomo Bakelite North America RX® 790 Fiberglass Reinforced Phenolic Novolac RX 790 is a fiberglass reinforced phenolic novolac compound, featuring a good balance of strength and toughness. Information supplied by Sumitomo Bak North America. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Solvay Specialty Polymers Ixef® 1313/0004 Polyarylamide, 40% Glass Fiber + Elastomer, DAM
(discontinued **)&l Impact modified. The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-2 |
| BASF Ultradur® B 4300 G10 50% Glass Filled PBT Description: Injection-molding grades containing 50% of glass fibers, for industrial parts, rigid, tough and dimensionally stable, for example for program switches, thermostat parts, small-motor hou.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| BASF Ultramid® N-265 NF3001 40% Mineral Filled PA66 (Dry) Ultramid N-265 NF3001 is a general purpose, 40% mineral reinforced PA6/6 that provides excellent flatness and dimensional stability in injection molding. |
|||