SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermally conductive mineral filled PA6 FR compounding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.79 g/cc | 0.0647 lb/in³ | ASTM D792 |
| Water Absorption | 0.23 % @Time 86400 sec |
0.23 % @Time 24.0 hour |
SABIC Method |
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0042 cm/cm @Time 86400 sec |
0.0042 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0058 cm/cm @Time 86400 sec |
0.0058 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 98.0 MPa | 14200 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.3 % | 1.3 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 13.28 GPa | 1926 ksi | 5 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.300 J/cm | 0.562 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.26 J/cm | 6.11 ft-lb/in | ASTM D4812 |
| Izod Impact, Unnotched (ISO) | 2.40 - 27.0 kJ/m² | 1.14 - 12.8 ft-lb/in² | ISO R179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.5 µm/m-°C @Temperature 40.0 - 120 °C |
22.5 µin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 85.4 µm/m-°C @Temperature 40.0 - 120 °C |
47.4 µin/in-°F @Temperature 104 - 248 °F |
ASTM E 831 |
| Thermal Conductivity | 0.980 W/m-K | 6.80 BTU-in/hr-ft²-°F | through-plane, ø80*3mm discs; ISO 22007-2 |
| 1.40 W/m-K | 9.72 BTU-in/hr-ft²-°F | through-plane, 10*10*3mm sample; ASTM E 1461-07 | |
| 1.80 W/m-K | 12.5 BTU-in/hr-ft²-°F | in-plane, ø25*0.4mm disc; ASTM E 1461-07 | |
| 2.38 W/m-K | 16.5 BTU-in/hr-ft²-°F | in-plane, ø80*3mm discs; ISO 22007-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-13 |
| 800 °C | 1470 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 1.00 - 3.00 mm |
1760 °F @Thickness 0.0394 - 0.118 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 4.84 @Frequency 1.00e+9 Hz |
4.84 @Frequency 1.00e+9 Hz |
ASTM ES 7-83 |
| Dielectric Strength | >= 10.0 kV/mm @Thickness 1.00 mm |
>= 254 kV/in @Thickness 0.0394 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0099 @Frequency 1.10e+9 Hz |
0.0099 @Frequency 1.10e+9 Hz |
ASTM ES 7-83 |
Users viewing this material also viewed the following:
- Multibase TPSiV™ 3011-85A Thermoplastic Silicone Vulcanizate
- Palm Labs Adhesives Turbo Fuse Series 440 (GEL) Rapid Bonding Adhesive
- NOVA Chemicals Novapol® LF-Y819-A LDPE Film Resin
- Overview of materials for Polycarbonate, Stainless Steel Fiber
- Solvay Specialty Polymers Hyflon® PFA M640 Perfluoroalkoxy (PFA)
- A. Schulman LP552-01 Narrow Molecular Weight Copolymer, High-Density Polyethylene
- Covestro Bayfill® 361 Polyurethane Semi-Rigid Foam, Conventional Catalyst, Open Pour, MDI-based 2-Component Liquid System
- Polyram PlusTek RA321G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant
- LTL Color Compounds ColorFast® FRPC200 Polycarbonate, Flame-Retarded
Copyright © lookpolymers.com All Rights Reserved