Toyobo VYLOPET® EMC310TU Injection Molding Polyester Resin, Warpageless, High cycles
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo VYLOPET® EMC310TU Injection Molding Polyester Resin, Warpageless, High cycles.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Coiled bobbinsMouthpiecesFeatures: High cyclesWarpagelessInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | MD |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 35 | 35 | CS-17; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 255 °C | 491 °F | By DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Thermal index; ASTM UL746B |
| 225 °C | 437 °F | Ball pressure temperature; IEC Method | |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.907 mm |
V-0 @Thickness 0.0357 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | Tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 250 - 399 V | 250 - 399 V | IEC Pub1.112, class 2; IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 255 - 265 °C | 491 - 509 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F |
Users viewing this material also viewed the following:
- Total Lacqtene® 2005 TN 59 HDPE pipe (discontinued **)
- Karina 804-06/115-CRM Blue PVC Compound
- SABIC Innovative Plastics ULTEM PW2100 PEI (Europe-Africa-Middle East)
- Sumitomo Chemical ESPOLEX® 4785 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ U-0294-L Blowing Agent Concentrate Based In PE
- A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene
- Ensinger Tecapeek® XP98 XRO Polyetheretherketone (PEEK), compression molded, 30% carbon fiber filled, x-ray opaque
- Fainplast Compounds AP 80 Flexible PVC, Flame Retardant Insulation
- Diapolyacrylate Acrypet® IR H70 Impact Modified PMMA
- Henkel SynCore HC 9875 Syntactic Film
Copyright © lookpolymers.com All Rights Reserved