- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 100 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 100 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 45H PC/ABS-blend, Flame Retardant Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 |
| Polykemi AB SCANMID 6 B32^ E Q30 Nylon 6, Glass Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D648 |
| Parker Chomerics PREMIER™ A230-FRHF EMI Shielding Plastic Description: PREMIER™ is the world’s first and most versatile commercially available conductive thermoplastic for real world EMI shielding solutions. It is a blend of PC/ABS thermoplastic polymer .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM HO TL10 Acetal Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(10%)Features: Lubricated, Good Wear Resistance and HomopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® POM HO TL2 Acetal Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(2%)Features: Lubricated, Good Wear Resistance and HomopolymerInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced PC/ABS that is used for the housing of mobile phone, wheel cap, rice cooker, electric iron etc., refrigerator door handle, panel etc.Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® GR-4017 ABS, Glass Filled Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced PC/ABS that is used for the housing of mobile phone, wheel cap, rice cooker, electric iron etc., refrigerator door handle, panel etc.Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75/Af |
| Solvay TECHNYL® A 216 S40 PA66, 40% glass spheres, DRY Description: Polyamide 66, reinforced with 40% of glass spheres, for injection molding.Available in: EuropeProduct Applications: TECHNYL ® A 216 S40 is used in all sectors of industry, offering a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | DIN 53461 |
| Polyram RamLloy PBB702 PC/ABS alloy, UV Stabilized UV stabilized PC/ABS alloy for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
| Polyram RamTal PMH2022 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 22.Information provided by Polyram. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Covestro Bayblend® KU 2-1474 Polycarbonate/ABS Blend Easier flowing than BAYBLEND T 64.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Covestro Bayblend® R-T 60 Polycarbonate/ABS Blend Recycled grade in which carefully reclaimed old parts and production rejects and/or scrap from all processes of manufacturing or processing undergo material recycling. Slightly decreased impact stre.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Covestro Bayblend® T 64 Polycarbonate/ABS Blend Easier flowing than BAYBLEND T 65 MN.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.35 mm |
212 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Chi Mei Acryrex® CM-205 PMMA High heat injection grade. It can resist high temperature. High mechanical strength.Applications: The indicator cover of scooter and automobile/sun glasses/digital watch cover.Features:Good Weather .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | 0.25 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 |
| Diamond Polymers ASA T-120 Description: ASA Weatherable Polymer, Injection Molding Grade, High Heat ResistanceInformation provided by Diamond Polymers, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Covestro Bayblend® KL 1-1430 Polycarbonate/ABS Blend Standard grade for cars.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Covestro Bayblend® KU 1-1446 Polycarbonate/ABS Blend Good cold impact strength and fuel resistance.Applications: Automotive industry (interior and body parts).Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated fr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Covestro Bayblend® T 65 Polycarbonate/ABS Blend High impact and notched impact strength, little risk of brittle fracture, high dimensional accuracy.Applications: Interior automotive components.Information provided by Bayer.As of 1 September 2015,.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM Test |
| BASF Ultramid® A27 E 01 PA66 (Dry) Ultramid A27 E 01 is a low-viscosity, general-purpose PA66 grade for compounding. It conforms to FDA requirements including, 21 CFR 177.1500,EU Directive 2002/72/EC, the German BfR recommendation ".. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 -1 & -2 flat |
| Asahi Kasei Tenac® SH510 Homopolymer Acetal Resin General purpose grade characterized by balanced flowability and mechanical properties.Information provided by Asahi Kasei Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1, 2 |
| Polyplastics Duracon® M140-44/M140S Acetal Co-polymer (POM), Standard, High flow DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Arkema Group Oroglas® V 825 T Acrylic
(discontinued **) OROGLAS V 825 T exhibits an excellent balance of properties including superior thermal resistance with an easy processing behavior.OROGLAS V 825 T is then the material of choice for automotive appli.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Delrin® 300CP BK642 Acetal Homopolymer
(Unverified Data**) Delrin® 300CP is a medium-high viscosity acetal homopolymer with improved thermal stability and an outstanding balance of ease of processing and part performance. This black is formulated to mainta.. |
|||