Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | ISO 75-C |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | ISO 75-C |
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | ISO 75-C |
Raschig Group MELOPAS® 6605 MP Melamine Cellulose reinforced Melamine molding compound. Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding be.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75 |
Raschig Group MELOPLAS® 150 MF Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75 |
Raschig Group MELOPLAS® 152 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 181 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf.. |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 183 MF Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 175 |
Perstorp Compounds Aminel FX Melamine Organically reinforced melamine material with excellent flow properties and high flexibility suitable for applications involving high complexity and surface demands.Information provided by Perstorp .. |
|||
Deflection Temperature at 8.0 MPa | >= 110 °C | >= 230 °F | ISO 175 |
Perstorp Compounds AMITEC 751 Melamine Perstorp dinnerware compression and injection grade. Porcelain like properties suitable for household applications.Information provided by Perstorp Compounds Inc. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-2 |
Hexion Bakelite™ PF 7592 Phenolic Formaldehyde Resin, Galvanized, Conductive
(discontinued **) Phenolic molding compound, inorganically/organically filled. Shrinkage fies compatible to values of UP 3310 and PF 2560. Electroplateable.Application areas: Chromium plated oven strips.Information.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-2 |
Hexion Bakelite™ PF 12404 Phenolic Formaldehyde Resin, High Surface Quality, Low Shrinkage
(discontinued **)& Phenolic molding compound, inorganically/organically filled, good dimensional stability, low shrinkage.Application areas: Housing parts for gas meter.Information provided by Bak AGBak AG became a pa.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-2 |
Hexion Bakelite™ PF 14694 Phenolic Formaldehyde Resin, High Surface Quality
(discontinued **) Phenolic molding compound, mainly organically filled, very soft flow for large molds.Application areas: Housing parts, heat shields, cookware fittings.Information provided by Bak AGBak AG became a p.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
Lanxess Durethan® BKV 30 000000 Nylon 6, 30% Glass Fiber 30% Glass fiber reinforced; injection molding grade |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
Lanxess Durethan® BKV 30 H2.0 901510 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers, good heat-ageing resistanceApplication Examples: pedal brackets, automotive front end structures |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
Lanxess Durethan® BKV 30 H3.0 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade with 30% glass fibers, good heat-ageing resistance |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
Lanxess Durethan® BKV 30 HTS 901510 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers, very good heat-ageing resistance |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1,-2 |
Lanxess Pocan® KU 2-7241 000000 PBT, 25% Glass Fiber PBT, 25% glass fibers, injection molding, flame retardant, improved impact strengthInformation provided by LANXESS. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® 1SBVX-30H LDS black PA1010-GF30 Product Description: Grilamid 1SBVX-30H LDS black is a 30% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is specifically optimized for the laser Direct Structuring techno.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LV-23 X ESD PA12-GF23 Product description: Grilamid LV-23 X ESD black is an antistatic Polyamide 12 injection moulding grade with 23 % glass fibre reinforcement. Main attributes are: antistatic with reisitivity < 10^6 O.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® XE 4106 black 9992 PA612-GF30 Product description: Grilamid XE 4106 black 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4106 are: low water absorpti.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® XE 4106 nat PA612-GF30 Product description: Grilamid XE 4106 natural is a 30% glass fiber reinforced, heat stabilized polyamide 612 injection molding grade. The main features of Grilamid XE 4106 are: low water absorptiong.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® TSC-10/4 EC black 9832 PA666-CF Information provided by EMS Grivory |
|||
Deflection Temperature at 8.0 MPa | 110 - 130 °C | 230 - 266 °F | Injection and Compression; ISO 75-C |
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing .. |
|||
Deflection Temperature at 8.0 MPa | 110 - 140 °C | 230 - 284 °F | Average value: 123 °C Grade Count:11 |
Overview of materials for Melamine-Phenolic Copolymer This property data is a summary of similar materials in the MatWeb database for the category "Melamine-Phenolic Copolymer". Each property range of values reported is minimum and maximum values of ap.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-2 |
Hexion Bakelite™ PF 8052 Phenolic Formaldehyde Resin, Resistant to High Temperatures
(discontinued **) Phenolic molding compound, glass fiber reinforced and inorganically filled. Excellent heat resistance with respect to surface finish and mechanical properties.Application areas: Pan handles, heat r.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LBV-50H FWA black 9225 PA12-GF50 Product Description: Grilamid LBV-50H FWA black 9225 is a 50% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combine.. |
|||
Deflection Temperature at 8.0 MPa | 110 °C | 230 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LBV-50H FWA nat PA12-GF50 Product Description: Grilamid LBV-50H FWA natural is a 50% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combined w.. |