Raschig Group MELOPAS® 6605 MP Melamine

Category Polymer , Thermoset , Melamine
Manufacturer Raschig Group
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group MELOPAS® 6605 MP Melamine.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cellulose reinforced Melamine molding compound. Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding behavior. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection molding Primary application: Molded parts in electrical engineering, arc chambersInformation provided by Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.50 - 1.70 g/cc
1.50 - 1.70 g/cc
ISO 1183
Apparent Bulk Density 0.550 - 0.750 g/cc
0.0199 - 0.0271 lb/in³
ISO 60
Water Absorption <= 2.00 %

@Temperature 23.0 °C,
Time 86400 sec
<= 2.00 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00800 - 0.0120 cm/cm
0.00800 - 0.0120 in/in
Injection; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength 60.0 - 85.0 MPa
8700 - 12300 psi
Injection; ISO 527
Modulus of Elasticity 5.00 - 8.00 GPa
725 - 1160 ksi
Injection; ISO 527
Flexural Strength 90.0 - 110 MPa
13100 - 16000 psi
Injection; ISO 178
Flexural Modulus 6.00 - 8.00 GPa
870 - 1160 ksi
Injection; ISO 178
Compressive Strength 200 - 250 MPa
29000 - 36300 psi
ISO 604
Charpy Impact Unnotched 0.700 - 1.10 J/cm²
3.33 - 5.23 ft-lb/in²
Injection; ISO 179/1eU
Charpy Impact, Notched 0.130 - 0.200 J/cm²
0.619 - 0.952 ft-lb/in²
Injection; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 - 35.0 µm/m-°C

@Temperature 50.0 - 100 °C
8.33 - 19.4 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Thermal Conductivity 0.400 - 0.500 W/m-K
2.78 - 3.47 BTU-in/hr-ft²-°F
ASTM E1461
Maximum Service Temperature, Air 135 °C

@Time 7.20e+7 sec
275 °F

@Time 20000 hour
IEC 60216/T1
160 °C

@Time <=180000 sec
320 °F

@Time <=50.0 hour
IEC 60216/T1
Deflection Temperature at 1.8 MPa (264 psi) 155 - 180 °C
311 - 356 °F
ISO 75-A
Deflection Temperature at 8.0 MPa 110 - 130 °C
230 - 266 °F
ISO 75-C
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Shrinkage 1.20 - 1.80 %

@Temperature 110 °C,
Time 605000 sec
1.20 - 1.80 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 - 1.00e+12 ohm-cm
1.00e+11 - 1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 - 1.00e+11 ohm
1.00e+10 - 1.00e+11 ohm
IEC 60093
Dielectric Constant 7.00 - 9.00

@Frequency 1.00e+6 Hz
7.00 - 9.00

@Frequency 1.00e+6 Hz
IEC 60250
11.0 - 16.0

@Frequency 100 Hz
11.0 - 16.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 20.0 - 25.0 kV/mm
508 - 635 kV/in
IEC 60243-1
Dissipation Factor 0.0300 - 0.0500

@Frequency 1.00e+6 Hz
0.0300 - 0.0500

@Frequency 1.00e+6 Hz
IEC 60250
0.300 - 0.500

@Frequency 100 Hz
0.300 - 0.500

@Frequency 100 Hz
IEC 60250
Arc Resistance 120 - 180 sec
120 - 180 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 15.0 - 25.0 °C
6.00 Month

@Temperature 59.0 - 77.0 °F
Descriptive Properties Value Comments
Glow wire flammability test 960/1
IEC 60695 2-12
Glow wire ignitability test 900/1
IEC 60695 2-13
Water Absorption <115 mg
24 hr, 23°C; ISO 62