Hexion Bakelite™ PF 7592 Phenolic Formaldehyde Resin, Galvanized, Conductive  (discontinued **)

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexion Bakelite™ PF 7592 Phenolic Formaldehyde Resin, Galvanized, Conductive  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Phenolic molding compound, inorganically/organically filled. Shrinkage fies compatible to values of UP 3310 and PF 2560. Electroplateable.Application areas: Chromium plated oven strips.Information provided by Bakelite AGBakelite AG became a part of Hexion in 2005.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Apparent Bulk Density 0.770 g/cc
0.0278 lb/in³
ISO 60
Linear Mold Shrinkage, Flow 0.0065 cm/cm
0.0065 in/in
Injection molding; ISO 2577
Mechanical Properties Metric English Comments
Flexural Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
Flexural Modulus 9.00 GPa
1310 ksi
ISO 178
Charpy Impact Unnotched 0.450 J/cm²

@Temperature 23.0 °C
2.14 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1/2 eU
Thermal Properties Metric English Comments
Deflection Temperature at 8.0 MPa 110 °C
230 °F
ISO 75-2
Shrinkage 0.300 %

@Temperature 110 °C,
Time 605000 sec
0.300 %

@Temperature 230 °F,
Time 168 hour
Injection molding; ISO 2577
Processing Properties Metric English Comments
Feed Temperature 60.0 - 75.0 °C
140 - 167 °F
Injection molding
Nozzle Temperature 80.0 - 100 °C
176 - 212 °F
Injection molding
Melt Temperature 80.0 - 100 °C
176 - 212 °F
Injection molding
Mold Temperature 160 - 190 °C
320 - 374 °F
Injection molding
160 - 190 °C
320 - 374 °F
Compression molding
Injection Pressure >= 15.0 MPa
>= 2180 psi
Compression and injection cavity mold pressure
Back Pressure 0.500 - 2.00 MPa
72.5 - 290 psi
Injection molding
Cure Time 0.167 - 0.333 min
0.00278 - 0.00556 hour
Per 1 mm of wall thickness, injection molding
0.333 - 0.667 min
0.00556 - 0.0111 hour
Per 1 mm of wall thickness, compression molding
Descriptive Properties Value Comments
Chromatic Spectrum All Colors
Creep Rupture Strength Very Good
Holding Pressure Approximately 40-60% of injection pressure
Media Resistance Very Good
Moisture Absorption 10 mg
ISO 62, 24 hours at 23°C
Reserves by Peak Temperature Very High
Thermal Expansion Very Slight