- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 183 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 183 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® ESD 7120 PRE-ELEC ESD 7120 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 7120 has been developed for inject.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ISO 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PS 1326 PRE-ELEC PS 1326 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Geloy XTWE265 ASA Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 3.20 mm |
183 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Geloy XTWE265 ASA (Europe-Africa-Middle East) Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Faradex MS002P PP (Asia Pacific) LNP* Faradex* MS002P is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, Exceptional Processi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 3.17 mm |
183 °F @Thickness 0.125 in |
injection molded specimen; ISO 75 |
| Phillips Sumika Marlex® CBF-300 Talc-Filled High Flow Thermoplastic Olefin
(discontinued **) Applications: Automotive exterior fasciasInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011. This product had been discontinued .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | |
| LyondellBasell Lupolen® 6021 D HDPE, Blow Molding Grade Easy flow, blow molding grade for small, rigid, thin-walled containers (up to 5 l), pots (up to 1 l), bottles and canisters (up to 5 l) for packaging mineral oil, antifreeze, brake fluid; drink bott.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical AF312B ABS, Flame Retardant Feature: Injection Molding, Flame RetardantApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 79-94-7 and 1309-64-4Information provided by LG Chemical.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical AF312C ABS, Flame Retardant Feature: Injection Molding, Flame RetardantApplication: Electric/Electronic Applications (TV, Monitor Housing) IT/OA deviceCAS No. 9003-56-9, 79-94-7 and 1309-64-4Information provided by LG Chemical.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical HIPS 460AF PS, Flame Retardant Description: Injection Molding, PS, Flame RetardantApplication: Electric Parts Requiring Flame RetardancyCAS: 9003-55-8, 25713-60-4, 84852-53-9 and 1309-64-4Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| Ineos A60-70-162 HDPE Ineos A60-70-162 is a high density polyethylene homopolymer, developed specifically for blow molding food containers on reciprocating screw-type equipment. It exhibits excellent processing character.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| Ineos H03G-05 Polypropylene Homopolymer Grade H03G-05 is a polypropylene homopolymer designed for BOPP applications and meet the requirements of the U.S. Food and Drug administration as specified in 12 CFR 177.1520.Applications:Food Packa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648-97 |
| Ipiranga Petrochem PCC 0412 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| LyondellBasell Pro-fax SR549M Polypropylene Random Copolymer, Clarified Primary Processing Method: Injection Molding and Injection Stretch Blow MoldingKey Features: clarified polypropylene random copolymer resin, superior clarity, good impact and rigidity balance, good .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY 63000CTC PC+POLYESTER (Asia Pacific) A permanent antistatic PC-Alloy compound that features transparency and superior cleanliness for advanced semiconductor packaging applications |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ISO 75-1/-2 |
| Styrolution Polystyrol 165 H GR 2 PS Description: Polystyrol 165 H is a high molecular weight, good flowing grade, often blended with high impact extrusion grades.Applications: In blends with high impact Polystyrene or Styrolux; thermo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Starex® VH-0819 ABS, Unreinforced FR Flame-retardant high flow ABS that can be used for the exterior of large TV and OA devicesInformation provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 83.9 °C | 183 °F | ASTM D648 |
| A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 83.9 °C | 183 °F | ASTM D648 |
| A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 83.9 °C | 183 °F | ASTM D648 |
| A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1579 Impact Grade Polypropylene DescriptionPolyfort® PP 1579H is an impact grade of polypropylene for use in parts which require good impact and good appearance in light-weight injection molded parts. Information provided by A. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C | 183 °F | ASTM D648 |
| Eastman Tenite 350A0096914 Propionate Natural Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 83.9 °C | 183 °F | Unannealed; ASTM D648 |
| Dow 6D20 Polypropylene Random Copolymer Resin OverviewConsistent processabilityGood regrind stabilityGood gloss and clarityLow odor and taste transferComplies with: U.S. FDA 21 CFR 177.1520 (c)3.1a, Europe EU-Directive 2002/72/ECDOW 6D20 Polypr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 83.9 °C | 183 °F | ASTM D648 |
| Aclo Accucomp ABS ABS801L Medium Impact Grade |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 83.9 °C | 183 °F | ASTM D648 |
| Aclo Accucomp ABS ABS811L Medium Impact Grade |
|||