- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 154 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 154 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648-95 |
| Multibase Multi-Pro® 2005 XRC Black 20% Filler Content Polypropylene Multi-Pro 2005 XRC is specifically designed for injection molded electronic industrial uses. This product shows higher heat distortion and notched izod than typical glass filled polypropylene. Thi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648-95 |
| Multibase Multi-Pro® 2010 X Natural 20% Filler Content Polypropylene Data provided by Multibase. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Eastar Copolyester K3000 PETG Copolyester
(discontinued **) EASTAR K3000 Copolyester is a cost effective, high-performance, water-clear material that provides the necessary performance for the appliance standards. Other desirable characteristics are good ch.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Tenite Butyrate 513E3720008 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 23%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648-82 |
| Micropol Microcene MC122 Metallocene Based Polyethylene Rotational Molding Powder Characteristics: reduced fusion, compacting, and crystallization times or lower oven temperatures; improved wall thickness control, improved impact resistance; low warpage; better creep resistance. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR (Asia Pacific) LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Cadence™ GS4 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | |
| Eastman Eastapak 9921 PET ISO data as provided by the manufacturer, Eastman Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Eastar GN120 Copolyester Applications:AppliancesConsumer electronicsPersonal care and cosmeticsStationary suppliesKey Attributes:High clarity and transparencyHigh flow copolyesterToughProduct Description: Eastar GN120 Cop.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Tenite Butyrate 485A2R30023 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 23%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Eastman Tenite Butyrate 565A3720023 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 23%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® FN718 BK230A Nylon 66
(Unverified Data**) Zytel® FN718 BK230A is a flexible, plasticizer free modified black polyamide 66 resin having good heat aging and chemical resistance.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Dow DMDA-8980 NT 7 High Density Polyethylene Resin DOW DMDA-8980 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as food containers. Information provided by Dow |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | unannealed; molded and tested in accordance with ASTM D 4101; ASTM D648 |
| Dow DS6D81 Polypropylene Resin DOW DS6D81 is intended for use as a heat seal coating on oriented polypropylene (OPP) film.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braskem in July 2011. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | Unannealed; ASTM D648 |
| Dow DS6D82 Polypropylene Random Copolymer Resin OverviewConsistent processabilityGood optical propertiesLow temperature heat sealComplies with U.S. FDA 21 CFR 177.1520 (c)3.1aDOW DS6D82 Polypropylene Resin is intended for use as a heat seal coati.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 67.8 °C | 154 °F | unannealed; molded and tested in accordance with ASTM D 4101; ASTM D648 |
| Dow DS6D82 Polypropylene Resin DOW DS6D82 is intended for use as a heat seal coating on oriented polypropylene (OPP) film.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braskem in July 2011. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM-D648 |
| Braskem GM5240PR HDPE High Density Extrusion Polyethylene GM5240PR is a high-density polyethylene compound specially developed for the manufacturing of pipes, underground conduits, and steel pipe coating. This resin is produced with bimodal technology and .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | ASTM-D648 |
| Braskem IH57 HDPE Injection Molding Polyethylene Copolymer IH57 is a high-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high stress cracking resistance with pr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | |
| Covestro Texin® 970U Urethane Thermoplastic Elastomer Key Features:UnfilledU.V. stabilized or stable to weatherSuitable processing methods:Injection moldingProfile extrusionSheet extrusionInformation provided by Bayer Polymers.As of 1 September 2015, B.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | |
| Arkema Group Kynar® FLEX 2800 PVDF
(discontinued **) Designation ISO 12086-VDF/HFP-K, EG1N, N. ?E7.D.G.B.C,, ? (3.5-7.5)Kynar FLEX PVDF are fluorinated thermoplastic copolymers.Outstanding characteristics of Kynar FLEX: chemical resistance, impervious.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 392 Ionomer Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 - 95.0 °C | 154 - 203 °F | Average value: 81.7 °C Grade Count:41 |
| Overview of materials for Cellulose Acetate Butyrate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Butyrate, Molded". Each property range of values reported is minimum and maximum value.. |
|||