SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR
| Category | Polymer , Thermoplastic , Polyurethane, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP TH0450A PUR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* TH0450A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.49 g/cc | 0.162 lb/in³ | ISO 1183 |
| 4.506 g/cc | 0.1628 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| 0.310 % | 0.310 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0104 cm/cm @Time 86400 sec |
0.0104 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0081 cm/cm @Time 86400 sec |
0.0081 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO 527 |
| 19.0 MPa | 2760 psi | ASTM D638 | |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527 |
| 20.0 MPa | 2900 psi | ASTM D638 | |
| Elongation at Break | 54.3 % | 54.3 % | ISO 527 |
| 78.6 % | 78.6 % | ASTM D638 | |
| Elongation at Yield | 26.6 % | 26.6 % | ISO 527 |
| 40.9 % | 40.9 % | ASTM D638 | |
| Tensile Modulus | 0.850 GPa | 123 ksi | 1 mm/min; ISO 527 |
| 0.920 GPa | 133 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 16.0 MPa | 2320 psi | ISO 178 |
| 18.0 MPa | 2610 psi | ASTM D790 | |
| Flexural Modulus | 0.660 GPa | 95.7 ksi | ASTM D790 |
| 0.760 GPa | 110 ksi | ISO 178 | |
| Izod Impact, Notched | 4.32 J/cm | 8.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 22.0 J | 16.2 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 18.0 J | 13.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 95.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 90.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 90.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 81.0 °C @Thickness 3.20 mm |
178 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 °C | 104 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 40.0 °C @Thickness 3.20 mm |
104 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Process Technologies Inc Silicone-Clear Sanitary Gasket
- Fiberfil® J-60/10/E Polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled
- Lucent Polymers 66-41 Nylon 66, Toughened
- Westlake EC800AA Low Density Polyethylene
- A. Schulman POLYBATCH™ Green 3012E Concentrate Based In Polyethylene
- Eagle Brass 706 Copper Nickel 10%, Extra Hard
- ExxonMobil Escorene™ UL 00119 Ethylene Vinyl Acetate Copolymer (European Grade)
- Dymax 3092 Solvent-Free Plastic Adhesive
- 3M Fluorinert™ FC-770 Electronic Liquid
- Nye Lubricants UniFlor 8921S (UF) Synthetic Oil
Copyright © lookpolymers.com All Rights Reserved