A. Schulman FORMION™ FI 392 Ionomer
| Category | Polymer , Thermoplastic , Ionomer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman FORMION™ FI 392 Ionomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.0060 - 0.010 cm/cm @Thickness 3.20 mm |
0.0060 - 0.010 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | Instantaneous; ISO 868 |
| Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
| Elongation at Break | 325 % | 325 % | ISO 527 |
| Flexural Modulus | 0.780 GPa | 113 ksi | Tangent; ISO 178 |
| Izod Impact, Notched (ISO) | 72.0 kJ/m² | 34.3 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 68.0 °C @Thickness 3.20 mm |
154 °F @Thickness 0.126 in |
ISO 75 |
Users viewing this material also viewed the following:
- Kinlead PL21 Lamination Grade BOPP Plain Film (thickness: 12 µm)
- Iran Petrochemical (PCC) 1922T Low Density Polyethylene
- ExxonMobil 16M Mobil DTE 10M Series
- A. Schulman PP 3482-01 Polypropylene Nucleated Homopolymer Polypropylene
- Eurotec® Tecodur® PB70 GR30 NL XA60 PBT, 30% glass fiber reinforced, flame retardant - halogen & red phosphorus, heat stabilized, natural
- Colorite Polymers MULTICHEM™ 6014 Vinyl-Urethane Blend
- ATI Wah Chang Zirconium Hydroxide, Zr(OH)4
Copyright © lookpolymers.com All Rights Reserved